From the perspective of convex pipe stress in the cap from hemispherical tube cap.
从受力角度看凸形管帽中从半球形管帽。
A pipe stress analysis software CAESARII is introduced to explore the methods for altering the force acting on the pipe.
介绍了管道应力分析软件CAESARII，分析了改变管道受力情况的方法。
The reasons and regularity of pipe stress corrosion cracking of some nuclear-powered steam generator was summarized, which caused serious leaking accident.
报道了某核动力系统蒸汽发生器，因管束的应力腐蚀破裂而发生严重泄漏事故的原因和规律。
After checking the pipe wall thickness, pipe stress and safety factors this batch of steel material has still complied with the requirements, while safety Surveillance should be enhanced.
通过管道壁厚、管道应力、安全系数的校核，表明该批钢材仍符合要求，但要加强安全监督。
The significance and methods of pipe stress analysis and thermal compensation in the design of process and thermal pipes and the commonly used thermal compensation equipments were described.
论述工艺及供热外部管道应力分析及热补偿的意义和方法，并介绍常用的热补偿装置。
Residual stress of longitudinal submerged arc welded pipe after welding is the major reason caused welded pipe stress corrosion crack, its stress level directly decide pipeline safety in service.
直缝埋弧焊管焊后残余应力是导致焊管应力腐蚀裂纹产生的主要原因。
Sensitive materials under low stress will suffer breakage which brings about large risk explosion of pressure bearing pipe and equipment is easily to be triggered causing major accident.
对于敏感性材料，在低应力水平下也会发生断裂，危险性很大，容易引发承压管道和设备的爆破，造成重大事故。
This standard describes the procedure for obtaining the Hydrostatic Design Stress (maximum working strength) for any thermoplastic pipe material at any practical temperature.
这个标准描述了获得流体静力设计应力(最大工作强度)的步骤，用于任何实际温度下的任何热塑塑料管道材料。
The thermal stress distribution of the stainless steel lined composite steel pipe prepared by centrifugal-SHS process was calculated by the finite element method under thermoelastic assumption.
用有限元方法计算了铝热离心法制备不锈钢内衬复合钢管过程中的残余热应力分布。
Body symmetry, in particular welded body structure, well under the stress from the pipe.
阀体对称，尤其是焊接阀体结构，能很好地承受来自管道的应力。
The distributions of the strain and the stress of the pipe are obtained by the numerical computation.
数值计算结果给出了管材在不同的拔制阶段的应变与应力分布。
Bring forward the strength conditions of the different pipe pars. Confirm the stress checking computations ways of the line pipes and corner pipes.
对于不同的管道部件提出了相应的强度条件，确定了直管段及转角管段的应力验算方法。
The temperature field and the thermal stress state of multilayer Wall pipe have a heavy effect on the reliability of structure.
多层圆管结构在不稳定导热过程中的温度场及其热应力状态，关系到结构的安全可靠性。
Therefore, it applies to a variety of stress path and the pipe connection.
故它适用于各种通径和压力的管道连接。
After the integrated analysis of each test result, it is proved that the pipe leakage failure is of stress corrosion damage.
在对各项试验结果进行综合分析之后确认，该管路泄漏失效为应力腐蚀破坏。
The results show that the cracking of the pipe is a kind of stress corrosion cracking.
分析结果表明，高压油管的开裂是应力腐蚀开裂造成的。
The result indicated that the failure cause of the stainless steel spiral pipe is the stress corrosion crack induced by Cl- ion.
结果表明，不锈钢盘管失效的原因是氯离子引起的应力腐蚀开裂所致。
The results show that the early failure of the cooling pipe was caused by the stress corrosion cracking in the components.
结果表明，冷却水管发生早期失效是由于构件发生应力腐蚀开裂所致。
Meanwhile, the intersection part of the bifurcation pipe is haunched, which helps to relief the stress concentration of the bifurcation pipe.
同时，经分析认为在岔管相贯部位采取了加腋措施，可有效缓解岔管部位的应力集中。
For HDPE pipe material, the weibull stress maybe an effective fracture parameter.
对于HDPE管道材料，威布尔应力可以作为有效的断裂控制参量。
The stress distribution of a curved pipe with an initial elliptic cross section under internal pressure was studied by using electric resistance strain method.
采用电阻应变测量技术研究了带有初始随圆度的弯管在纯内压作用下的应力分布。
The method of stress analysis for pipe with special joints including Y joint and taper - taper joint is indicated through the analysis of vacuum transfer line.
本文通过对减压转油线的应力分析，说明了特殊形状三通管道（包括Y形三通、裤形三通） 的应力分析方法和过程。
The allowable stress of the pipe material shall be chosen from the data of GB 50316 Design Specification for Industrial Metal Piping.
管子材料的许用应力可按GB 50316《工业金属管道设计规范》中的数据选用。
Temperature Stress in open reinforced concrete pressure pipe usually is one of the important reasons why their longitudinal cracks-occur in use.
外露式钢筋混凝土压力管道的温度应力，常是某些这类管道在运用期内产生纵向贯通裂缝的重要原因之一。
In this article, it shows formulas to calculate bending moment, shear strength and maximum stress of heat tracing pipe and shell body.
首先给出了半管加热管及壳体的弯距、剪力及最大应力计算公式。
In stress analysis of petrochemical pipe line, the secondary stress check is the one of basic strength check.
石化管道应力分析中，二次应力的校核是最基本的强度校核之一。
This paper applies the three-dimensional finite element method to the analysis of the stress for steam expanding vessel with tangential pipe, and the stress distribution has been obtained.
采用三维有限元方法对蒸汽扩容器与切向接管联接的关键部位进行了应力分析，获得了该部位的应力分布。
This paper applies the three-dimensional finite element method to the analysis of the stress for steam expanding vessel with tangential pipe, and the stress distribution has been obtained.
采用三维有限元方法对蒸汽扩容器与切向接管联接的关键部位进行了应力分析，获得了该部位的应力分布。