There are three main interior structure defects in the preparation of aluminum foam with melt foaming process such as free-bubble-layer at the bottom, partial free-bubble-zone and heat crack.
泡沫铝常见的内部缺陷主要有底部无泡层、局部无泡区和内部热裂纹。
The results show that the partial unmelted region, casting defect structure and secondary crack form in the welding seam, which result in the low stress breakage of the samples.
结果表明：在焊缝区域内存在着局部未熔区以及铸造疏松组织和二次裂纹等缺陷，这是导致试样低应力断裂的根本原因。
The results show that the partial unmelted region, casting defect structure and secondary crack form in the welding seam, which result in the low stress breakage of the samples.
结果表明：在焊缝区域内存在着局部未熔区以及铸造疏松组织和二次裂纹等缺陷，这是导致试样低应力断裂的根本原因。