The high-temperature oxidation behavior and the possibility of protection for Mo-based ceramets in air were studied experimentally.
试验研究三种钼基金属陶瓷材料在空气中的高温氧化行为及防护的可能性。
The results of the research works show that oxidation behavior of PAN-based CF is related with its morphology and graphite crystallite parameter.
研究结果表明，PAN基炭纤维的氧化特性与其石墨微晶参数和表面形貌密切相关。
This indicated that the oxidation behavior in two phase alloy can be deeply affected by the shape, size and spatial distribution of the two phase particles.
可见，在二元双相合金中，合金的氧化行为与合金的组织形态、大小和分布密切相关。
In this paper, oxidation behavior of carbon materials was illustrated and the methods taken for oxidation resistance at high temperature were briefly introduced.
本文阐述了炭材料的氧化行为，简单介绍了炭材料的各种氧化防护方法。
The main problems existed in the present MR suspensions include: lack of methods to improve the shear stress, bad anti-settlement behavior and anti-oxidation behavior.
磁流变液目前普遍存在磁致剪切应力提高手段有限、磁性颗粒容易沉降、抗氧化性差等问题。
The dissociative adsorption and oxidation behavior of HCOOH on Pt was investigated by cyclic voltammogram (CV) and in-situ surface enhanced Raman spectroscopy (SERS) techniques.
采用循环伏安法和电化学原位表面增强拉曼光谱 （SERS）技术研究甲酸的解离吸附与氧化行为 。
The voltammetric behavior and oxidation mechanism of loperamide were investigated by cyclic voltammetry and coulometry at a multi-wall carbon nanotube paste electrode (MCNT-PE).
用循环伏安法和控制电位库仑法研究了洛哌丁胺在多壁碳纳米管碳糊电极(MCNT - PE)上的伏安行为及反应机理。
The results shows the capacity of the anode oxidation membrane decreases with the increasing of oxidation potential, and there exists relationship between impedance and behavior anode polarization.
提出了钽的氧化反应式及反应控制步骤；得出其氧化膜电容量随着氧化电位的增加而减少，阻抗与阳极极化行为存在相关关系。
The results shows the capacity of the anode oxidation membrane decreases with the increasing of oxidation potential, and there exists relationship between impedance and behavior anode polarization.
得出其氧化膜电容量随着氧化电位的增加而减少，阻抗与阳极极化行为存在相关关系。
The effect of lanthanum oxide on thermo-oxidative degradation behavior of LLDPE was studied by thermogravimetry, oxidation induction time measurements, rheological and TG-FTIR analyse.
通过热失重、氧化诱导期、流变分析和热重-红外联用分析等方法研究了氧化镧对LLDPE热氧分解行为的影响。
The behavior of oxidation for the intravenous fat emulsion was determined under the presence of nitrogen, oxygen or air at different temperature.
测定了静脉脂肪乳剂分别在充氮、充氧及空气存在条件下于不同温度下的氧化规律。
The results show that there exist great differences in surface morphology, oxidation species and flotation behavior of galena ground with ceramic or iron media.
结果表明，采用瓷介质与铁介质磨矿时，方铅矿表面形态、表面氧化产物及浮选行为存在明显差异。
The electrochemical behavior of the methanol oxidation on the platinum electrode with different concentration H2SO4 solution was studied by using cyclic voltammetry.
用循环伏安法研究在不同酸度的硫酸钠溶液中，甲醇在铂电极上氧化的电化学行为。
The behavior of oxidation-induced stacking faults (OSF) in NCZ and CZ silicon single crystal was investigated.
采用直拉法生长普通和掺氮硅单晶，研究不同含氮浓度的晶体中氧化诱生层错（OSF）的行为。
The wettability by water and oxidation resistance of the coated graphite powders were greatly improved and the electro-kinetic behavior of the coated graphite powders was similar to that of Al2O3.
氧化铝包覆石墨复合粉体与水具有良好的润湿性，其表面特性与氧化铝相似，并且抗氧化性能得到较大的改善。
The wettability by water and oxidation resistance of the coated graphite powders were greatly improved and the electro-kinetic behavior of the coated graphite powders was similar to that of Al2O3.
氧化铝包覆石墨复合粉体与水具有良好的润湿性，其表面特性与氧化铝相似，并且抗氧化性能得到较大的改善。
应用推荐