During 18 years of trails and hardships, Jinbo has put up 8 wholly-owned white fused alumina production lines, 3 mullite production lines and 2 magnesia alumina spinel production lines.
在18年的风雨历程之中，金渤按计划陆续投产了8条全资白刚玉生产线、3条莫来石生产线、2条镁铝尖晶石生产线。
Micropowder of mullite is manufactured by gap mill.
采用环缝磨制备了莫来石微粉。
So in studies of the activity of fly ash influence of mullite can be ignored.
因此在研究粉煤灰活性时，可以不考虑莫来石的影响。
The XRD result shows that the main crystalline phase of the ceramic is mullite.
射线衍射分析结果表明，材料的主晶相为莫来石。
Corundum-mullite Board: it is made by high sintering corundum and mullite together.
刚玉—莫来石棚板：是以电熔刚玉、莫来石复合成型经高温烧结而成。
The substructure and the fracture process of mullite ceramics were studied by TEM and SEM.
用透射电镜和扫描电镜研究了莫来石陶瓷的亚结构特征和断裂过程。
The porous mullite ceramics showed a uniform pore size distribution and a porosity of 96.22%.
这种多孔莫来石纤维陶瓷具有较均匀的孔分布，并且孔隙率高达96·22 %。
Some methods about preparation of mullite whisker at home and abroad are reviewed in this paper.
本文对国内外制备莫来石晶须的合成方法作了简要的综述。
The effect of sintering technology of mullite on its bending strength was studied systematically.
系统研究了合成莫来石烧结工艺对其抗弯强度的影响。
The aging process of mullite short fibre reinforced ZL109 composites was studied via hardness test.
通过测试硬度的方法，对莫来石短纤维增强ZL 109复合材料的时效析出行为进行了研究。
A fibre reinforced mullite insulating material has been developed under simple processing condition.
引入耐火纤维，在相对简单的工艺条件下研制了纤维增强莫来石隔热材料。
Used for corundum bricks , mullite bricks , silicate bricks masonry in blast furnaces , hot air stoves .
用于高炉、热风炉砌筑刚玉砖、莫来石砖、硅线石砖、低蠕变高铝砖。
At first, the effect of particle size and additions of andalusite on mullite-corundum materials were studied.
首先，研究了红柱石的粒度和加入量对莫来石-刚玉材料性能的影响。
Secondly, the effect of particle size and additions of kyanite on properties of mullite-corundum was studied.
其次，研究了蓝晶石的粒度和加入量对莫来石-刚玉材料性能的影响。
The tensile stress in matrix introduced by mullite particles made the cracks incline to extend into the matrix.
由莫来石颗粒引入的基体拉应力使裂纹倾向于向晶内扩展。
The rupture of corundum-mullite materials was controlled by crack at room temperature and creep at high temperature.
刚玉莫来石材料的断裂在室温下由裂纹扩展控制，在高温下由蠕变机制控制。
The furnace body is welded by profile steel and plates and the studio in the furnace shell is made of hi-temp mullite.
炉体是采用型钢、板材焊接而成的炉壳，炉壳内的工作室采用高温莫来石砌筑成型。
The preparation of the aluminum titanate-mullite kiln furniture using aluminum titanate-mullite composite was studied.
并采用合成的钛酸铝—莫来石复相材料进行了钛酸铝—莫来石窑具的制备研究。
This is mainly because of the effect of volumetric expansion which occurs when kyanite powder is transformed into mullite.
这主要是由于蓝晶石细粉向莫来石转化时发生的体积膨胀效应所致。
Mullite gels are excellent precursors for preparing fine mullite. Mullite gels consist of monophasic gel and diphasic gel.
莫来石凝胶是制备超细莫来石的优良先驱物，主要分为单相和双相凝胶。
Fine mullite powder was synthesized by sol-gel process with tetraethoxysilane (TEOS) and aluminium nitrate as raw material.
以正硅酸乙酯和硝酸铝为原料，采用溶胶-凝胶法制备出了超细的纳米莫来石。
XRD and SEM techniques were used to characterize the mullite solid solution synthesized from waste aluminum slag and kaolin.
采用XRD和SEM等测试手段对用铝厂废渣和高岭土合成的莫来石材料进行微观结构表征。
At last, this paper studied the effect of particle size and additions of sillimanite on properties of mullite-corundum materials.
最后，研究了硅线石的粒度和加入量对莫来石-刚玉材料性能的影响。
The polycrystalline structure of mullite-cordierite polyphase material and its contents were determined by XRD and SEM, respectively.
采用XRD和SEM法确定莫来石-堇青石复相材料的晶相结构及其含量。
The effect of the sintering temperature and the mullite content on the dielectric properties and the bending strength has been studied.
研究了烧结温度和莫来石含量对复合材料的介电性能和抗弯强度的影响。
This paper introduces the application effect of multicrystal mullite refractory fiber in walking furnace with unity of beam and bottom.
介绍了多晶莫来石纤维在梁、底组合步进式加热炉上的使用效果。
The casted door brick for reverberatory furnace which introduced mullite grains has an obvious longer service life than the imported brick .
通过引入烧结莫来石颗粒料，浇注成型生产的莫来石质反射炉炉门砖，使用寿命明显高于进口砖。
The residual stresses in the alumina matrix and on the mullite particles as well as their effect on crack growth were analyzed by modelling.
通过模型分析了氧化铝基体和莫来石颗粒的应力状态及其对裂纹扩展的影响。由莫来石颗粒引入的基体拉应力使裂纹倾向于向晶内扩展。
Mullite - cordierite composites with various mullite contents and microstructures were prepared by liquid phase sintering and by hot pressing.
由热压和液相烧结方法制得了具有各种莫来石含量和显微结构的莫来石—堇青石复合体。
The properties of corundum-mullite-zirconia grogs made by reaction-sintering process and their carbon-bonded materials have been investigated.
研究了反应烧结制备的锆刚玉莫来石系熟料及其碳结合材料的性能。