The effect of UPPE molecular weight, NVP/UPPE ratio, BPO/UPPE ratio on the crosslinking temperature, setting time, compressive strength and compressive modulus was investigated.
研究了聚合物分子量、交联剂N-乙烯基吡咯烷酮与引发剂过氧化苯甲酰的含量对最高交联温度、固化时间、压缩强度及压缩模量的影响。
A kind of high strength and high modulus fibre was prepared by means of plasticized melt spinning of high molecular weight polyethylene (HMWPE) with wax blend and high stretch ratio.
采用石蜡增塑高相对分子质量PE后纺丝并经高倍拉伸制备高强高模纤维。
A kind of high strength and high modulus fibre was prepared by means of plasticized melt spinning of high molecular weight polyethylene (HMWPE) with wax blend and high stretch ratio.
采用石蜡增塑高相对分子质量PE后纺丝并经高倍拉伸制备高强高模纤维。