However, the research on composite mechanism of polymer modified mortar is almost scarce.
对聚合物的作用机理研究几乎还是空白。
Tests were made on flexural, compressive, bonding and tensile strengths of styrene-acrylic latex modified mortar.
通过试验对苯丙胶乳改性砂浆的抗折强度、抗压强度、粘结强度及抗拉强度进行了研究。
This paper introduces the physical mechanical properties of waterproof and anticorrosive polymer modified mortar.
介绍聚合物防水防腐砂浆的物理力学性能。
The result shows that both early compressive and flexural strength of the polymer modified mortar are low, but the late strength increases steadily.
结果表明：改性砂浆早期抗压和抗折强度较低，后期强度有较大持续的增长；
The adhesion strength of hydroxyethyl methyl cellulose modified mortar and ethylene copolymer modified mortar were studied at different curing condition.
研究了羟乙基甲基纤维素和乙烯基共聚物两种聚合物干粉改性砂浆在不同养护条件下的粘结抗拉强度。
The function mechanism and applications of polymer modified mortar are discussed. The problems and future application of polymer modified mortar are pointed out.
探讨了聚合物砂浆的作用机理以及应用，介绍了聚合物砂浆在应用中存在的问题，并据此对聚合物砂浆的应用进行了展望。
The effects of interfacial treatment modes on the bonding properties between asphalt modified polyurethane joint material and cement mortar were investigated.
就界面处理方式对沥青改性聚氨酯接缝材料和水泥砂浆黏结性能的影响进行了研究。
The test results indicated that the bond splitting tensile strength of modified fly ash mortar was best in joint materials of sorts.
试验结果表明，各种接缝面材料中，粉煤灰改性砂浆的劈裂抗拉强度最大，效果最好。
We reinforce the mortar by blending with surface modified polypropylene fiber.
研究了表面改性丙纶对水泥砂浆制品的增强作用。
Modified effect was studied on fresh mortar and hardens mortar with bentonite.
研究了膨润土对新拌砂浆和硬化砂浆的改性效果。
The properties of cement mortar modified by hydroxyethyl methyl cellulose and vinyl co-polymer were studied.
研究了羟乙基甲基纤维素和乙烯基共聚物两种聚合物干粉改性砂浆加水搅拌后的性能。
The results indicated the JME modified epoxy mortar was optimal material for erosion and abrasion resistant material for the repair of damaged composites.
JME改性环氧树脂砂浆是高速水流抗冲磨修补的理想材料。
After the replacement with modified concrete of chloroprene latex and epoxy cement mortar, no damages have been found after two years of operation.
通过采用氯丁胶乳改性混凝土及环氧砂浆面层进行更新改造，投用两年多，至今没有任何损坏。
With increasing of modified EPS powders size, the segregation phenomenon of mortar became seriously, water retention, workability and bending strength decreased.
随着EPS颗粒粒径的增大，砂浆的分层度增大，保水性、和易性及抗折强度降低。
The invention discloses a modified vitrified micro bubbles thermal insulation mortar and a preparation method thereof.
本发明公开了改性玻化微珠保温隔热砂浆及其制备方法。
The study show that not only elasticity and tenacity properties of modified epoxy injecting mortar have been improved, but better compressive strength and tensile strength also amilisrated as well.
这种改性的环氧树脂注浆材料不仅弹性、韧性得到大大提高，而且仍具有较高的抗压与抗拉强度、高粘结性。
A new type of modified epoxy cement mortar has been developed, for which a testing analysis is made for the application to the bonding reinforcement for concrete.
研制了一种新型改性环氧水泥浆，对其在混凝土粘结补强中的应用进行试验分析。
Tests of concrete slab strengthened by steel plate with epoxy mortar leveling, adhesing and corering for structural behavior and tests of modified epoxy mortar for material behavior are carried out.
在工业环境下钢筋混凝土板受到严重侵蚀，可采用结构胶泥找平后粘覆钢板进行加固。
Waste rubber powder is modified by different modifiers, then fiber reinforced rubberized mortar with a certain function is developed by adding different amount of waste rubber power and fiber.
将废橡胶粉以不同的改性剂进行表面改性，以不同取代量掺入水泥砂浆，并采用纤维增强，制备了具有一定功能性的纤维增强废橡胶粉水泥砂浆。
Waste rubber powder is modified by different modifiers, then fiber reinforced rubberized mortar with a certain function is developed by adding different amount of waste rubber power and fiber.
将废橡胶粉以不同的改性剂进行表面改性，以不同取代量掺入水泥砂浆，并采用纤维增强，制备了具有一定功能性的纤维增强废橡胶粉水泥砂浆。