The tensile strength, elongation and hardness of T10 steel subjected to magnetic field quenching and to high temperature tempering were separately increased by 28%, by 8.
与经普通淬火和高温回火的相比，经磁场淬火和高温回火的T10钢的抗拉强度提高了28%，断后伸长率提高了8。
In addition, the magnetic field quenching will increase the resistance of the T10 steel to tempering because of a large amount of dispersed carbides in the steel after magnetic field quenching.
此外，磁场淬火还提高了T10钢的抗回火能力，这是由于磁场淬火后的钢中含有大量弥散碳化物所致。