The tensile strength, elongation and hardness of T10 steel subjected to magnetic field quenching and to high temperature tempering were separately increased by 28%, by 8.
与经普通淬火和高温回火的相比,经磁场淬火和高温回火的T10钢的抗拉强度提高了28%,断后伸长率提高了8。
Transverse rupture strength, Rockwell a hardness, magnetic saturation induction and magnetic coercivity of samples sintered in vacuum or by sinter-HIP were measured.
测试了真空烧结和低压烧结试样的抗弯强度、洛氏硬度、磁饱和度和矫顽磁力。
Improve the testing equipment, magnetic detection machines and hardness.
检验设备完善,有磁粉探伤机和硬度计。
It is proved that the hardness of ferro magnetic materials can be measured by the Barkhausen Noise Method.
本文提出采用巴豪森噪声法测量铁磁材料的硬度。
Experimental results indicated that there is a monotonic relationship between the hardness of ferro magnetic materials and Barkhausen Noise strength, MP.
试验结果表明,巴克·豪森噪声强度值mp与铁磁材料的硬度值之间存在单调的关系曲线。
Regardless of DC or AC magnetic field, the hard phase in weld metal overlay is fine and distributed "the hexagon" in optimum parameters, then hardness and wear extent in weld metal overlay are higher.
在最佳的磁场参数作用下,无论是直流磁场还是交流磁场,堆焊层中硬质相细小且成“六角形”分布,此时堆焊层金属的硬度和磨损量均达到最佳状态。
It has a high hardness after quenched and has excellent corrosion resistance (with magnetic).
淬火后硬度高,耐蚀性好(有磁性)。
Different metallographic constitutions in castings have their corresponding magnetism and hardness. The more the content of pearlite, the harder and the lesser magnetic the casting is.
铸件金相组织与硬度及磁性有对应关系,铸件的珠光体多则硬度高、磁性差。
The performance of synergistic scale inhibition was investigated in different water temperature, magnetic field intensity, water hardness and concentration.
研究了不同温度、磁场强度、水质硬度及加药量下的协同阻垢性能。
This paper deals with the influences of pulsed magnetic field on the depth, microstructure and hardness of the nitrided layer and the thickness of the compound layer.
本文研究了脉冲磁场对气体氮化的氮化层深度、化合物层厚度、氮化层组织及其硬度的影响。
Stainless steel exterior 430 (18/0) possesses good hardness and contains carbon, thus has magnetic and can be used on induction cooker.
外层不锈钢430(18/0),硬度较高,含有碳成分,因此有磁性,可用在电磁炉上,而且不锈钢430的光洁度也非常好。
The relationship between hardness depth and magnetic coercive force was studied. Based on this relationship we develop a new type of electromagnetic nondestructive measurement instrument (DWY - 1).
通过分析磁矫顽力与淬硬层深度之间的关系,试制了一种电磁无损检测仪(DWY-1)。
The relation of magnetic properties and hardness of wire rod with its cooling rate on Stelmor line was investigated.
研究了盘条的磁性、硬度与其在斯太尔摩线上冷速间的关系。
This paper discussed the influence of the magnetic field intensity H and welding current I on the hardness and the wear resistance of the Co-based alloys surfacing lager.
系统地研究了磁场强度H和焊接电流I对钴基堆焊合金堆焊层硬度和耐磨性的影响,发现当磁场强度H和焊接参数相匹配时,焊缝组织才能获得最佳的细化效果。
The results show that transverse magnetic field can refine the primary crystallization structure by electromagnetic stirring and improve the ultimate strength and hardness of the welded joint.
结果表明,通过外加横向磁场对熔池进行搅拌,可以使焊缝晶粒得到细化,进而使其抗拉强度和硬度等力学性能得到改善;
The results show that transverse magnetic field can refine the primary crystallization structure by electromagnetic stirring and improve the ultimate strength and hardness of the welded joint.
结果表明,通过外加横向磁场对熔池进行搅拌,可以使焊缝晶粒得到细化,进而使其抗拉强度和硬度等力学性能得到改善;