The influences of chromium content on the hardness, impact toughness and corrosion resistance of low carbon alloy steel were studied using om and hardness tester.
利用光镜、显微硬度计研究了铬含量对低碳合金钢组织、硬度、冲击韧度及耐均匀腐蚀性的影响。
The corrosion wear resistance of low chromium white cast iron increases when the silicon content increases in it.
而增加含硅量后的低铬白口铸铁的腐蚀磨损耐磨性将比普通白口铸铁的高。
The effect of carbon and chromium content on the impact fatigue resistance and impact abrasion resistance of pearlitic low chromium cast iron has been investigated in this paper.
研究了碳、铬含量对珠光体基体低铬铸铁冲击疲劳抗力及冲击磨损性能的影响。
Magnetic stainless steels that have a low carbon content and contain chromium as the main alloying element, usually between 13% and 17%.
有磁性的不锈钢碳含量较低，铬是其中主要的合金元素，通常含量为13%到17%。
The effect of Si content on the corrosion wear resistance of low chromium white cast iron in the slurry with Cu2+ ion was studied by three-body corrosion wear test.
而增加含硅量后的低铬白口铸铁的腐蚀磨损耐磨性将比普通白口铸铁的高。
The effect of Si content on the corrosion wear resistance of low chromium white cast iron in the slurry with Cu2+ ion was studied by three-body corrosion wear test.
而增加含硅量后的低铬白口铸铁的腐蚀磨损耐磨性将比普通白口铸铁的高。