The engendering rule of organism of liquidus casting aluminum alloy A356 at different heat preservation temperature, different heat preservation time was investigated.
研究了液相线铸造A35 6铝合金在不同保温温度、不同保温时间下的组织形成规律。
Studying the nearby liquidus semi -continuous casting technics of A356alloy by means of orthogonal test.
选用正交试验法,研究了A356铝合金近液相线半连续铸造工艺参数的影响。
The casting and remelted microstructures of ZL201 alloy cast by liquidus semi-continuous casting(LSC)were studied.
研究了近液相线半连续铸造ZL201合金的微观组织及其在二次加热过程中的变化。
The near-liquidus semi-continuous casting (LSC) process was used in casting ZL201 alloy.
采用近液相线半连续铸造的方法制备了ZL201铝合金半固态锭坯。
The solid/liquid phase transformation of ZL201 aluminium alloy in near liquidus semi-continuous casting was simulated using multiscale simulation technique.
用多尺度模拟方法研究了近液相线半连续铸造中的ZL201合金的液/固相变。
In the liquidus nearby, the grains size becomes coarse with increasing of casting temperature.
在液相线附近,晶粒尺寸随着浇铸温度的降低而逐渐减小并呈球化的趋势。
In the liquidus nearby, the grains size becomes coarse with increasing of casting temperature.
在液相线附近,晶粒尺寸随着浇铸温度的降低而逐渐减小并呈球化的趋势。