The effects of strain rate and engineering strain on liquid phase segregation in the process of semi-solid metal forming have been revealed in this paper.
揭示了半固态金属成形过程中应变率和变形量对液相偏析影响的规律。
The results showed that the solid liquid phase zone, temperature interval and segregation degree may be obviously enlarged with increasing s content so as to reduce the hot plasticity of the alloy.
结果表明，随着S含量的增加，导致固液两相区、温度范围和偏析程度明显加大，引起合金的热塑性降低。
The results showed that the solid liquid phase zone, temperature interval and segregation degree may be obviously enlarged with increasing s content so as to reduce the hot plasticity of the alloy.
结果表明，随着S含量的增加，导致固液两相区、温度范围和偏析程度明显加大，引起合金的热塑性降低。