According to the elastic theory, this paper gives partition Law of stress and quantitative answers over the overlap joint weld on skirted support.
利用弹性理论，分析推证出了裙式支座搭接焊逢内的应力分布规律及其定量解答。
For AZ31 and AZ61 magnesium alloy, effects of activating fluxes with hybrid component on weld forming in the a - TIG butt joint welding of are studied.
对接实验针对AZ31和AZ61镁合金材料，研究了在A-TIG焊中混合成分的活性剂对焊缝成形的影响。
The rupture reasons of tube joint weld of the stainless steel pressure meter are analyzed. It is characteristic of stress corrosion cracking and inter granular fracture.
分析了不锈钢压力表管接头焊缝开裂的原因，认为此种开裂具有应力腐蚀开裂、沿晶断裂特征。
The results show that after TIG arc remelting treatment, the T-joint weld toe area can improve the shape of the weld toe, however, the area till shows a tensile residual stress state.
数值计算结果表明：T型接头焊趾区经过TIG电弧重熔处理后，虽然能够改善焊趾的形状，但该部位仍呈拉伸残余应力状态。
The purpose of weld guide bending test is to detect plasticity of welding joint, welding process and surface defects of materials.
焊缝导向弯曲试验的目的是检查焊接接头的完好性和塑性以及材料的焊接工艺和表面缺陷。
By comparing backgouging of plasma arc with carbon arc to the welded joint of 13-5 martensitic stainless steel, the backgouging of plasma arc is proved feasible for the full penetration weld.
通过对13 -5型马氏体不锈钢焊接接头进行等离子弧清根及碳弧气刨清根的比较，证明等离子弧清根对全焊透焊缝实施背面清根是可行的。
Improvement of elongation of joint is related to weaker cool deformation degree of heat affect zone (HAZ) and uniformity of strength and stress level between weld and base metal.
接头延伸率的改善同热影响区冷变形程度的减弱及焊缝强度、应力水平同母材趋于一致有很大关系。
The paper studies the fatigue failure probabilistic model of the weld zone in welded joint using probabilistic fracture mechanics and reliabilitistic analysis methods.
本文采用概率断裂力学方法和可靠性分析方法，针对压力容器焊接接头的组织不均匀特点，研究了焊缝区疲劳失效概率模型。
All butt, grooved t, and corner joints shall be complete joint penetration weld joints.
所有对接、T型槽和弯管接头都要完全侵入连接到焊接接头上。
Weld fracture components were analysed by SEM and EDS, joint defect and fracture mechanism were also researched.
利用扫描电子显微镜和能谱分析(EDS)对焊缝断口进行成分分析，研究焊接接头的焊接缺陷及断裂机制。
Its results show that with decreasing the relative width of under-matching weld metal, the tensile strength of welding joint increase.
结果表明：随低强焊缝金属相对宽度变小，接头抗拉强度增大；
Therefore, the weld joint is the most significant point in the weld-quality-controlling.
因此，该处对于焊接质量的控制就成为很重要的位置。
The tests show: there are steady arc burning, fully fused weld joints, good connection between base metal and weld joint, no air bubble, cracks etc.
试验过程电弧燃烧稳定，焊接接头充分熔透，母材与焊缝连接良好，未见气孔、裂纹等缺陷。
The results showed by verification that, outside the range of weld joint, the calculation theory proposed by this paper is reliable.
验证结果表明，除了焊缝区之外，本文提出的计算理论是可靠的。
The invention has good weld joint molding effect and uniform weld joint reinforcement.
本发明焊缝成型效果好，焊缝余高均匀。
The corrosion behavior of austenite stainless steel weld joint in the different acidic medium was studied.
研究了奥氏体不锈钢焊接接头在不同酸性介质中的腐蚀行为。
The main region of invalidation of the weld joint between different steels is commonly in fusion zone during welding or serving.
异种钢焊接接头在焊接时或使用期间，发生失效的主要区域通常在熔合区。
To deal with corrosion at weld joint, shielded inert gas are will be used and the insulation grade raised.
采用非熔化极惰性气体保护焊，并提高焊口绝缘等级，克服焊口的晶间腐蚀。
The weld size was controlled according to the definition of leg on the corner joint and DL/T869—2004 (power plant welding technical regulation), which led to the effective thickness was insufficient.
按目前大多数人认可的角接接头焊脚的定义，根据DL/T869—2004《火力发电厂焊接技术规程》去控制焊接尺寸，会出现焊缝有效厚度不足的问题。
The micro shear test could give a new way to evaluate the mechanical properties in weld joint of aluminium alloy.
微型剪切试验为铝合金焊接接头力学性能的评定提供了一个新途径。
Since laser weld is narrow, and the anode protection effect of zinc on the base metal was not destroyed, the joint has good corrosion resistance.
激光焊缝窄，基材锌层阳极保护作用得以保存，激光焊接板仍具有较好耐蚀性。
The result shows that, as the crack stands on melt line of welded joint, the values of J-integral are different from those of both all-base and all-weld metal.
结果表明，无论是平面应变还是平面应力条件下，焊接接头J积分值都与全母材和全焊缝材料不同；
The stress concentration state of weld joint on a tube socket containing defects exceeding grade after long term service has been evaluated by using the magnetic memory test (MMT).
用磁记忆检测(M MT)法评价了含超标缺陷管座角焊缝长期服役后的应力集中状况。
Along with the wider use of monolithic joint in the design of long span steel truss Bridges, the fatigue of weld details under traffic loads gradually attracted more attention of the architects.
随着整体节点正逐渐在大跨度钢桁架桥设计中被采用，在交通荷载作用下焊接局部的疲劳问题日益引起人们的重视。
A choke shape design is used for obtaining the satisfactory weld joint.
采用缩口的接触型式，能获得满意的电阻焊接头。
The reason for preventing the weld joint from cold cracking with this kind of insulator to keep the weldment cooling slowdown is discussed also.
探讨了硅酸铝保温缓冷焊接条件下能防止焊接冷裂纹的原因。
The reason for preventing the weld joint from cold cracking with this kind of insulator to keep the weldment cooling slowdown is discussed also.
探讨了硅酸铝保温缓冷焊接条件下能防止焊接冷裂纹的原因。