The results show that the treatment makes the interlaminar shear strength of the composite increased 17.5% and the linear ablation rate decreased 58.6%.
得出，该方法是提高复合材料层间剪切强度和抗烧蚀性能的有效方法，它可使层间剪切强度提高17．5 ％ ，线烧蚀率减小58．6 ％ 。
In order for the solution of the laminated plates and shells to ensure interlaminar continuity of the physical variables, the transfer matrix technique was used.
针对层合板壳问题，为了保证各层之间物理参量的连续性，进一步应用了状态转移矩阵技术。
In the range of incident velocities near to the perforation limit velocity (V50), this mechanism depends on thickness and interlaminar shear strength of composite plate.
在接近穿孔极限速度的入射速度(V50)范围内，这一机制依赖于复合材料板的厚度和中间层剪切强度。
In this paper, the interlaminar stress distributions of symmetric composite laminates with a hole are predicted by the three-dimensional elastoplastic finite element method.
本文用三维弹塑性有限元法计算了含圆孔对称复合材料层板的层间应力分布。
The three loading type are studied and analyzed, and calculated with finite element method for compressive stresses and interlaminar shear stresses distribution on 1-3 face.
本文对这三种加载形式进行了研究和分析，并用有限元素法计算了这三种加载形式在1—3面内的压应力和层剪应力的分布。
It was concluded that the interlaminar tensile strength of the composite is dominated by the bonding strength of the interface between fiber and matrix, not by lay-up orientation.
结果表明：该复合材料层间拉伸强度较少受到铺层取向的影响，而由纤维与基体的界面结合强度所控制。
With the methods of the pre-heating before welding, controlling the interlaminar temperature and the heat treatment after welding, the welds that satisfy the quality specifications can be available.
通过焊前预热、层间温度控制及焊后热处理等手段获得了满足质量要求的焊缝。
With the methods of the pre-heating before welding, controlling the interlaminar temperature and the heat treatment after welding, the welds that satisfy the quality specifications can be available.
通过焊前预热、层间温度控制及焊后热处理等手段获得了满足质量要求的焊缝。