These catalytic mechanisms of interfacial agent in some chemical reactions are micelle catalysis and phase transfer catalysis.
表面活性剂催化化学反应过程的机理有胶束催化和相转移催化。
Bond plane is the tache of weakness for the new and old concrete bond structure when withstanding shear force and tension. Appropriate interfacial agent can improve bond strength.
当承受剪力和拉力时,粘结面是新老砼粘结结构受力的薄弱环节,使用合适的界面剂可以提高其粘结强度。
As interfacial agent, the mix of cement and fly ash can improve the adhesive shear strength. After planted reinforced bar, the shear strength of new and existing concrete increases greatly.
而在界面上植入抗剪钢筋后,能大幅度提高了新老混凝土的粘结抗剪强度。
A newly developed phosphorus silicate material, SJT-B, is an effective auxiliary agent which slows down corrosion, prevents scale formation and reduces interfacial tension.
助剂是一种磷硅酸盐化学添加剂,它具有良好的缓蚀防垢和降低界面张力效果。
After high silica fiber is treated by coupling agent, excellent interfacial cohesion and flexural strength of super-hybrid composite are obtained.
偶联剂处理使高硅氧纤维与树脂基体的粘结强度增加,从而提高复合材料的弯曲强度。
The influence of concentration of KH-570silane coupling agent solution to the pull-off bonding strength of concrete at the new-to-old interfacial layer was studied through experiment.
试验探讨了KH- 570硅烷偶联剂溶液浓度对新老混凝土粘结界面层拉拔强度的影响。
Slow-released microcapsule anti-mosquito finishing agent was prepared using polyurethane as wall and anti-mosquito finishing agent HLQZ as core by interfacial polymerization.
研究了自制乳化剂、芯壁比、反应温度以及催化剂用量对合成防蚊整理剂的影响。
STJ-B aiding agent is a newly developed phosphorus silicate chemical additives, which has favorable effects on slowing down the erosion, preventing the scales and re-ducing the interfacial tension.
助剂是一种磷硅酸盐化学添加剂,具有良好的缓蚀防垢和降低界面张力的效果。
The results showed that:(1)the mechanical property of coupling agent-treated fire retardant was improved since the interfacial combination between the fire retardant and matrix was enhanced;
结果表明:经偶联剂处理过的阻燃剂,由于增强了其与基体的界面结合力,从而使其力学性能得到提高;
The results showed that:(1)the mechanical property of coupling agent-treated fire retardant was improved since the interfacial combination between the fire retardant and matrix was enhanced;
结果表明:经偶联剂处理过的阻燃剂,由于增强了其与基体的界面结合力,从而使其力学性能得到提高;