The shape and stability of the "miniature slag pool" affect the thickness of slag skin and the ESR ingot surface quality.
微渣池的形状和稳定性影响着钢锭渣皮厚度的变化和钢锭表面质量。
The main basis of deciding ESR ingot surface quality is that there is a cylinder part or not in ingot side freezing forward position -metallic molten pool.
钢锭侧面凝固前沿位置即金属熔池具有无圆柱部分是判断电渣锭表面质量优劣的基本依据。
Scab. An imperfection in the form of a shell or veneer, generally attached to the surface by sound metal. It usually has its origin in an ingot defect.
结疤。通常由钢锭缺陷引起的、附着在完好金属表面上的薄壳状或镶片状缺欠。
Ingot defects may be broadly classified into internal flaws and surface flaws. Internal flaws are caused by shrinkage.
钢锭缺陷广义上可分为内部缺陷和表面缺陷。内部缺陷是因收缩引起的。
During ingot casting, control of casting speed is an important measure to improve the surface and inner qualities.
铸锭时控制钢液的注流速度，是改善和提高钢锭表面和内部质量的重要工艺措施。
Ingot defects may be broadly classified into internal flaws and surface flaws.
钢锭缺陷广义上可分为内部缺陷和表面缺陷。
On the contrary, the surface imperfections, such as oscillation and subsurface segregation etc, found in DCC ingot, cause the mechanical properties drop largely.
相反，普通连续铸造锭表面因存在振动痕和亚表面偏析等铸造缺陷，力学性能大大降低。
Thus a high quality ingot with good surface finish is produced.
这样具有良好表面光洁度的高质量钢锭就生产出来了。
Thus a high quality ingot with good surface finis. is. produced.
这样具有良好表面光洁度的高质量钢锭就生产出来了。
The surface and inner qualities of aluminum alloy ingot by electromagnetic casting (EMC) have been investigated and compared with those of the direct casting (DC) one.
分析了电磁铸造铝合金铸坯的表面和内部质量，并与普通连续铸造铸坯进行了对比。
The methods to improve the quality of the surface of extrusion materials by removing the defects on the surface layer of casting ingot are reviewed in this paper.
本文综述了清除铸锭表层缺陷，以提高挤压材表面质量的方法。
The results show that the current flows during VAR from crucible wall to the electrode via the surface of the ingot melt pool, and the currents in the crucible base and the ingot base are almost zero.
结果表明：重熔电流从坩埚壁经熔池表面流回电极，铸锭和坩埚底部几乎没有电流；
These ingot molds can produce a slab which is subjected to a number of thickness reductions, sometimes associated with surface treatments and machining, depending on the various processes used.
这些锭模可以生产板坯，根据所使用的各种方法，该板坯经历多次有时与表面处理和机械加工相关的厚度减小。
Influence of different crystallizer and cover agents on surface quality of round Cu ingot with P deoxidation in channel induction furnace was expounded.
论述了有芯工频感应电炉生产磷脱氧铜圆锭不同结晶器和不同铸造保护气氛对铸锭质量的影响。
The service life of the boron surface alloying grey cast iron ingot mold is 43% longer than that of high Mn low si grey cast iron ingot mold.
试验结果表明：铸渗硼灰铸铁钢锭模比同类灰铸铁钢锭模的使用寿命提高43％。
The infrared thermometer is mounted on the mechanical scanning mechanism so as to bi-dimensionally scan the surface of the casting ingot.
所述红外测温仪安装在机械扫描机构上，对铸坯表面进行二维扫描测温；
The infrared thermometer is mounted on the mechanical scanning mechanism so as to bi-dimensionally scan the surface of the casting ingot.
所述红外测温仪安装在机械扫描机构上，对铸坯表面进行二维扫描测温；