The rheological model of segmented function of high temperature deformation resistance was established. The calculated results by the rheological model were in good agreement with experiments.
并且建立了高温变形抗力的分段函数流变模型，该模型计算结果与试验值吻合较好。
High temperature deformation behavior of Ti-6Al-4V (TC4) was studied by using the constant rate tensile test under different deformation conditions in MTS high temperature tensile experimental system.
采用普通工业TC4板料，在MTS高温拉伸试验系统上进行了不同变形条件的恒速拉伸试验，研究材料的高温变形行为。
The results show that thermal compensation in non-irradiant areas could reduce the temperature gradient of mirror for high-power laser, and then could decrease the thermal deformation significantly.
结果表明有效的热补偿对镜面变形峰谷值有很大的影响，在非光照区进行热补偿可以大大降低镜体的温度梯度，从而明显减小镜面变形的峰谷值。
This paper discusses the two indexes, dynamic stability and relative deformation, that evaluate the high temperature stability of the asphalt mixture by rutting test.
本文通过车辙试验讨论了衡量沥青砼热稳性的两个指标：动稳定度和相对变形。
In this paper, based on systematic test on different bitumen mixtures of gradation, the deformation behaviour of asphalt mixtures is analyzed under high temperature.
本文通过对不同级配形式的沥青混合料的系统试验研究，全面分析了沥青混合料高温变形特性。
High strength, long service life, the temperature can reach 300 degrees Celsius and above deformation.
强度高，使用寿命长，耐温可达300摄氏度以上不变形。
The lithosphere beneath this area is associated with high temperature, low strength and intensive rheological stratification, and the lower crust is characterized by ductile flow deformation.
岩石圈具有温度高、强度低和强烈流变分层等特征，且下地壳表现为韧性流动变形。
Excellent resistance to oil, high temperature resistance, weather resistance are good, but the mechanical strength, compression deformation rate and water resistance is slightly worse.
对油品有极佳的抵抗力，耐高温、耐候性均佳，但机械强度、压缩变形率及耐水性稍差。
Large amounts of deformation can lead to smaller ferrite grains which can balance the high temperature soaking effect.
另外大量之高温塑性变形可以产生较小之肥粒铁晶粒这样可以抵消高温热浸温度所造成之晶粒粗大效应。
The change of the components leads to high temperature stress, as well as remarkable shrinkage and deformation; also, its characteristics induce friability and fissility of concrete.
现代混凝土组分的变化导致了温度应力高、收缩变形大，早强和高强也引发了混凝土的早裂和高脆性。
The stress and deformation of chimney and other special tube elements under fire and cyclic high-temperature loads are presented.
分析了烟囱与陶瓷管道特殊构件受明火燃烧及循环高温荷载条件下的应力与变形。
The resin produced by the flame-retardant products with high strength and mechanical properties, thermal deformation temperature, curing speed, and good soak.
该树脂所生产制品具有很高的阻燃性能和机械强度，热变形温度高，固化速度快，浸透性好。
On the contrary, the larger railway embankment deformation will be brought if the railway embankment is high and the area has high average annual air temperature.
相反，在该地区年平均温度较高，路基高度也较大的情况下，冻土路基的变形较大，这也和监测结果相符合。
The silicon and fluorine rubber with high temperature resistance, low compression permanent deformation, and high tear strength properties can meet the water sealing gasket requirements.
采用耐高温、低压缩永久变形、高抗撕裂硅、氟橡胶可以满足该部位需耐高温、耐冷却水的要求。
The principle of the internal faults (cavities and cracks originated from inclusion) recovery was investigated in the plastic deformation by using the method of physical modeling at high temperature.
论文采用钢试件高温模拟方法对热加工过程中易引起大型锻件内部探伤超标的孔洞型缺陷、夹杂性裂纹等缺陷的修复规律进行了探讨。
The high temperature creep deformation of certain material used in aerial engines lamina was detected by means of high temperature moire interferometry in this paper.
利用高温云纹干涉法对航空发动机叶片定向结晶材料的高温蠕变进行了测试，获得该材料不同主方向的高温蠕变性质和规律。
The spheroidizing grow, in isothermal spheroidizing process, of carbides formed from deformation under high temperature in, hypoeutectic white cast iron is studied.
对亚共晶白口铸铁经高温形变后所获得的碳化物在等温球化过程中球化长大进行了研究。
The fiction can prevent large loads caused by high pressure and high temperature from spreading, which can result in severe deformation in a short part of tubing.
摩擦力大小和方向的改变，将使因高温高压产生的较大载荷无法向远处扩散，从而引起油管局部严重变形。
During forging forming process, temperature affects the pattern of metal deformation considerably, especially in the forming process at high temperature.
锻件成形过程中，非稳态、不均匀的温度场对金属的塑性流动有很大的影响，尤其是高温成形过程。
Mechanism of damage of clay pot for utensil glass melting, such as softening deformation at high temperature, corrosion by molten glass, crack by thermal shock, etc was studied.
对熔化器皿玻璃等的粘土质坩埚使用中的高温软化变形、玻璃液侵蚀、热震开裂等损毁机制进行了分析研究。
Triaxial repeated load creep tests are employed to evaluate the influence of high temperature and heavy load on the deformation property of AC-20 asphalt mixture.
为评价高温和重载对沥青混合料变形特性的影响，对AC - 20级配的沥青混合料进行三轴重复荷载蠕变试验研究。
Void growth behavior plays an important role in the deformation, damage and rupture of the nickel-base single crystal superalloys at high temperature.
在高温状态下，镍基单晶超合金的变形、损伤及断裂分析中，孔洞的长大都起着主要的作用。
The creep-deformation and corrosion atmosphere accelerates wear failure course at the high temperature.
在高温下的蠕变和腐蚀气氛加快了磨损失效过程；
The new material is not only oil resistant, but also has fairly great improvement in performance of high temperature resistance, fatigue resistance and permanent deformation resistance.
新材料不仅具有耐油性，在耐高温性、耐疲劳性和抗永久变形性方面也有较大幅度的提高。
The results show that the increase of cyclic frequency would decrease high temperature fatigue lifetime of the alloy and result in different deformation mechanism.
结果表明，循环频率的增加会导致合金高温疲劳寿命的下降及不同的变形机制。
The superplasticity research was carried out under constant temperature compression deformation for salt-bath cyclic quenched and high frequency hardened T10A steel.
采用盐浴加热循环淬火和高频感应加热淬火对T10A钢进行组织超细化预处理，然后在恒温压缩变形条件下进行超塑性研究。
The wood of poplar is compressed, then the compression deformation is fixed by high temperature steam and heating.
采用高温水蒸气处理和加热处理固定大青杨木材压缩变形，并对两种处理结果进行比较。
A nitrogen heat treatment method of nozzles was proposed for the sharp wear, evident high temperature creep deformation of the nozzles for sulfur atomization.
针对硫磺雾化喷嘴存在磨蚀快、高温蠕变明显的现象，提出了喷嘴氮化热处理的方法。
This paper deals with creep deformation and stresses of a spherical pot under high temperature and uniform internal pressure.
本文对高温、均匀内压作用下球罐的蠕变变形和应力进行了探讨。
This paper deals with creep deformation and stresses of a spherical pot under high temperature and uniform internal pressure.
本文对高温、均匀内压作用下球罐的蠕变变形和应力进行了探讨。