Using these diagnostics it is shown that pin abrasive tests do not represent high stress abrasion in any industrially-relevant sense.
利用这些诊断结果表明，针磨料测试并不代表高应力磨料磨损在任何工业相关的常识。
However, we have found no evidence of such a phenomenon in ball mills, and instead the observed behaviour is attributed to high stress abrasion in the service environment.
但是，我们发现，没有证据显示，这种现象在球磨机，而不是观察到的行为，是由于高应力磨损，在服务环境。
Pin abrasive tests are widely thought to simulate high stress abrasion, but in reality they grossly over-estimate service lives of white iron mill liners compared to pearlitic steel liners.
针磨料测试被普遍以为是模仿高应力磨损，但实践上它们严重高估效劳生命地白口铁磨内衬比拟珠光体钢内衬。
The main failure form of pulping scroll cover is high stress grinding abrasion accompanying corrosive abrasion.
磨浆段螺旋套主要的失效形式为高应力磨料磨损，同时伴有腐蚀磨损。
Under high stress or low stress abrasion working conditions, high Cr white cast iron can be used just after it having been air quenched.
高应力磨料磨损或低应力磨料磨损工况条件下，高铬白口铸铁空淬后不须回火可直接应用。
Under high stress or low stress abrasion working conditions, high Cr white cast iron can be used just after it having been air quenched.
高应力磨料磨损或低应力磨料磨损工况条件下，高铬白口铸铁空淬后不须回火可直接应用。