The results showed that the higher internal stress and serious carbide network in the banded carbide in the inner roll body were the main causes of heavy back-up roll stationary cracking.
结果表明，辊身心部较高的内应力和在带状碳化物中存在严重的网状碳化物是造成大型支承辊置裂的主要原因。
Heavy back-up roll fractures spontaneously when it is placed.
大型支承辊在放置时自然断裂。
It has been analysed the causes for the heavy surface spalling of back-up roll for a finishing mill. The result shows that the main causes are gas hole, shrinkage and bad heat treatment.
对连轧机精轧支承辊大面积剥落的原因进行了深入的分析，结果表明，轧辊内部的缩孔、气泡及热处理不当是造成轧辊表面剥落的主要原因。
It has been analysed the causes for the heavy surface spalling of back-up roll for a finishing mill. The result shows that the main causes are gas hole, shrinkage and bad heat treatment.
对连轧机精轧支承辊大面积剥落的原因进行了深入的分析，结果表明，轧辊内部的缩孔、气泡及热处理不当是造成轧辊表面剥落的主要原因。