General natural graphite was modified by liquid-phase oxidation method using cerium sulfate as an oxidant.
用硫酸铈作氧化剂，通过液相法将普通的天然石墨进行氧化改性。
The results of the research works show that oxidation behavior of PAN-based CF is related with its morphology and graphite crystallite parameter.
研究结果表明，PAN基炭纤维的氧化特性与其石墨微晶参数和表面形貌密切相关。
The current efficiency of the Br - oxidation on graphite electrodes is normally over 80% with the highest being 88. 5%.
溴离子在石墨电极上氧化的电流效率一般在80%以上，最高可达88.5%。
Expanded graphite is a soft porous material which is produced by natural squama graphite by means of oxidation, inserting, watering, dryness and expansion.
膨胀石墨是一种柔软、疏松多孔的物质，它是由天然鳞片石墨经氧化、插层、水洗、干燥及高温膨化而得到的。
The carbon graphite material prepared by the means of improving the oxidation resistance of the basic body materials and impregnated with phosphates had better oxidation resistance.
采用改善炭石墨基体材料抗氧化性能和浸渍磷酸无机高分子复合盐的内外结合的方法，制备的石墨材料具有较好的抗氧化性能。
The coating protection could prevent the graphite rotator for molten Alpurification from the oxidation and prolong its service life effectively.
采用涂料保护法能防止铝熔体净化用石墨转子的氧化，有效地延长其使用寿命。
Graphite phase is deposited in the process of ZL108 micro arc oxidation.
在ZL 10 8微弧氧化过程中，实现了石墨相的沉积。
The consumption of the graphite anode in the calcium molten salt electrolysis process is analyzed, which includes oxidation consumption and physics damage.
分析了钙熔盐电解过程石墨阳极消耗的两个因素 ，即主要有氧化消耗和物理破损 。
The methods of modification included the surface covering of graphite with a layer of disorganized carbon or a film of appropriate metal, surface oxidation, mechanical grinding and doping.
修饰与改性方法包括形成包敷层和金属层、表面氧化、机械研磨以及掺杂等方法。
The wettability by water and oxidation resistance of the coated graphite powders were greatly improved and the electro-kinetic behavior of the coated graphite powders was similar to that of Al2O3.
氧化铝包覆石墨复合粉体与水具有良好的润湿性，其表面特性与氧化铝相似，并且抗氧化性能得到较大的改善。
The novel material having high temperature sealing ability and oxidation resistance can be obtained by impregnated carbon-graphite with MB-04 impregnant.
用MB—04浸渍剂对碳—石墨材料进行浸渍处理，可获得既具有耐高温密封性能，又具有抗氧化特性的新材料。
The behaviour, usage and applied effectiveness of oxidation resistant coatings for graphite electrode were reviewed.
本文介绍了石墨电极用防氧化涂料的特性、防氧化机理、使用方法及应用效果。
A voltammetric and control potential electrolysis investigation of the direct electro-oxidation decarboxylation of D-gluconate ion to D-arabinose on spectroscopic graphite electrode is reported.
报导了用伏安法和恒电位电解法在光谱石墨电极上直接电氧化d -葡萄糖酸钠合成d -阿拉伯糖的研究结果。
The palladium alloy nanowire arrays were electrodeposited on the surface of highly oriented pyrolytic graphite by successive three pulses of potential or current (oxidation, nucleation and growth).
用连续三脉冲(氧化、成核和生长)电势或电流在高定向石墨表面电沉积钯合金纳米线阵列。
The results show that the chemical vapor deposited carbon can apparently improve the oxidation property of fine grain graphite, especially for high temperature deposition.
结果表明：化学气相沉积炭，尤其是在高温沉积情况下，可明显提高细颗粒石墨材料的氧化性能，但对于粗颗粒石墨氧化性能的影响较小。
The results show that the chemical vapor deposited carbon can apparently improve the oxidation property of fine grain graphite, especially for high temperature deposition.
结果表明：化学气相沉积炭，尤其是在高温沉积情况下，可明显提高细颗粒石墨材料的氧化性能，但对于粗颗粒石墨氧化性能的影响较小。