Corrosion test shows that proper rare earth addition enhance the general corrosion sensitivity.
腐蚀试验表明，添加微量稀土元素可增强抗点腐蚀敏感性。
The result showed that the general corrosion took place in the pins and shaft made from 304 steel in ammonium sulfate mother liquor.
结果表明：由304钢制造的销子和阀轴在硫铵母液中产生了全面腐蚀。
Results showed that the general corrosion rate of steel was higher accompanied with different extent local corrosion under research range of parameters.
结果表明：在所研究的参数范围内，材料表现出较高的均匀腐蚀速率，且伴有不同程度的局部腐蚀。
In general, most of the thermoplastic materials offer high impact strength, corrosion resistance, and easy processing with good flow characteristics for molding complex designs.
一般而言，大多数热塑性材料具有较高的抗冲击强度、耐腐蚀性以及良好流动性使其容易加工而适于复杂成型设计。
Corrosion and scaling are the general problems in developing and using geothermal resource.
腐蚀与结垢是地热开发利用中普遍存在的问题。
The mechanism and general influence factors of sulfide stress corrosion cracking (SSCC) of chemical equipment made of high strength steel are summarized.
系统的综述了高强钢化工设备硫化物应力腐蚀开裂机理及常规的影响因素。
General term for compounds or materials that slow down or stop an undesired chemical change such as corrosion oxidation or polymerization drying skinning mildew growth etc.
延缓或阻止不希望发生的化学变化的化合物或材料的通称，例如腐蚀、氧化或聚合、风干、油漆起皮、霉菌生长等现象。
The system and general design, functional models and characteristic of a concrete resist reinforcing sulfate corrosion expert system are described.
阐述了混凝土抗硫酸盐侵蚀专家系统的系统设计、总体设计、功能模块及其特点。
However, like general reinforcement concrete structure, a main problem in prestressed concrete is the poor corrosion resistance of steel tendon which may lead to the lower durability construction.
然而和普通钢筋混凝土一样，预应力混凝土中存在的一个主要问题是钢筋抗腐蚀能力弱，结构耐久性差。
Through the analysis of corrosion forms of carbon steel water cooler in the fertilizer plant of Urumqi General Petrochemical Works, the various factors leading to corrosion were described.
通过对乌鲁木齐石化总厂化肥厂碳钢水冷却器的腐蚀形态分析，阐述了发生腐蚀的诸多因素。
Discussing the anti - corrosion coating program of the general suspension bridge 's steel box beam protective railings and steel wire cables in the situation of heavy corrosion.
论述了在重腐蚀条件下，一般悬索桥的钢箱梁、防护栏杆和钢丝主缆的防腐蚀涂装方案。
The general idea of developing corrosion control of weapon equipment systematically in remanufacturing Engineering was outlined.
提出了系统性开展装备腐蚀控制再制造的思路。
The company has been committed to the fluorine control valve and fluorine valve general research and production, has become a field of strong corrosion valve professional manufacturers.
公司一直致力于衬氟控制阀和衬氟通用阀的研究与生产，现已成为强腐蚀领域阀门的专业生产厂家。
The more general impurity acid corrosion faster.
一般来说杂质越多酸蚀速度越快。
Electrophoresis process can make parts of the salt fog spray process time from 240 hours of general upgrade to 1000 hours, greatly enhance the ability of vehicle corrosion preventive.
电泳工艺能够使工件的耐盐雾时间从普通喷涂工艺的240小时提升到1000小时，大大提升车辆的防腐防锈能力。
Electroplating trough: bearable, storage solutions, the pilot line chemicals general considerations intensity, corrosion resistant, heat resistance, and other factors.
电镀槽：可承受，储存电镀药水的槽体，一般考虑强度，耐蚀，耐温等因素。
The rational aspects of the fluxing model as well as the general characteristics existing in high temperature gaseous corrosion and hot corrosion are considered in the electrochemical model.
根据热腐蚀的特点，吸收盐熔模型的合理成分，并考虑到热腐蚀与高温气体腐蚀的共性，提出热腐蚀的电化学模型。
The rupture in the middle of bulk cargo is due to the corrosion and fatigue of components in long term usage, which leads the section modulus to reduce and the general longitudinal strength to weaken.
船舯断裂的主要原因之一是船体构件因长期受到腐蚀、疲劳等作用而造成船舯剖面模数降低，进而削弱了总纵强度。
Saltwater (sea) ordinary steel in sodium chloride solution and sea water, salt water corrosion rate is not too high in general have to the use of paint protection;
盐水（海水）普通钢铁在氯化钠溶液和海水、咸水中腐蚀率不太高，一般须采用涂料保护；
The heat stability and corrosion resistance of the unsaturated polyester resin were tested. The property is better than that of general purpose unsaturated polyester resin.
对该不饱和树脂的热稳定性及耐腐蚀性进行了实验，其性能优于通用型不饱和树脂。
This article describes anti - corrosion coating support system of the general suspension bridge, and also describes the process of coating and what the matters should take attention in constructing.
介绍了一般悬索桥防腐涂装配套体系。阐述了涂装工艺流程和施工时需要注意的事项。论述了在重腐蚀条件下，一般悬索桥的钢箱梁、防护栏杆和钢丝主缆的防腐蚀涂装方案。
This article describes anti - corrosion coating support system of the general suspension bridge, and also describes the process of coating and what the matters should take attention in constructing.
介绍了一般悬索桥防腐涂装配套体系。阐述了涂装工艺流程和施工时需要注意的事项。论述了在重腐蚀条件下，一般悬索桥的钢箱梁、防护栏杆和钢丝主缆的防腐蚀涂装方案。