The gel fraction increases with absorbed dose.
随着吸收剂量的增大，凝胶含量增加。
The presence of monomer is almost no contribution to ultimate gel fraction of polyethylene.
它对聚乙烯的极限凝胶分量几乎没有贡献。
At same dose, the gel fraction increases with PVA concentration and gradually reaches a stabs turation state.
同一吸收剂量下，随着PVA浓度的增加，其凝胶含量先上升后趋于饱和。
The effect of the radiation condition on the gel fraction, crosslinking regulation, and the network molecular weight were studied.
本文研究了辐射条件对硫化硅橡胶的凝胶分数、交联规律和交联网格分子量的影响。
The experimental results showed that gel fraction of the PEO graft hydrogel films depended mainly on irradiation dose and concentration of the polymers.
实验结果显示，PEO接枝水凝胶膜的凝胶分数主要依赖于辐射剂量和聚合物浓度。
When the PEO molecular weight increased, the gel fraction, the degree of swelling and the hardness of the PEO hydrogel films increased obviously as well.
当PEO分子量增加时，其水凝胶膜的凝胶分数、膨胀度和硬度亦明显增加。
The effect of peroxide proportion on gel fraction of crosslinked PE and the relationship between gel fraction and the mechanical properties of the compound were investigated.
探讨了过氧化物用量对交联聚乙烯凝胶含量的影响，以及凝胶含量与材料力学性能的关系。
The effect of peroxide content on mechanical properties and gel fraction was researched, as well as the effects of carbon black, ZnO and antioxidant on properties of material.
探讨了过氧化物用量对交联聚乙烯凝胶含量的影响，以及凝胶含量与材料力学性能的关系。
The experimental results show that the irradiation dose and mass fraction ofthe polymer do not produce a significant effect on the gel fraction, of the PEO R-150 water-swollen hydrogel films(P>0.05).
结果显示，PEOR-150溶胀水凝胶膜的交联密度随辐射剂量的增加略有增加，但无统计学意义（P>0.05）；聚合物质量分数对其交联密度的影响无显著性差异（P>0.05）。
Biliary protein was isolated and purified by ammonium sulfate fraction and Sephadex G-75 gel filtration column chromatograph from complex pig bile.
采用了凝胶过滤结合硫酸铵沉淀法从异常复杂的胆汁中成功分离出一种蛋白质。
The hydrogenated NBR with the hydrogenation degree of80%and the gel mass fraction of 3.1%was obtained.
通过加入对苯二酚，降低了加氢产物的凝胶质量分数，制得了氢化度为80%，凝胶质量分数为3.1%的HNBR。
The hydrogenated NBR with the hydrogenation degree of80%and the gel mass fraction of 3.1%was obtained.
通过加入对苯二酚，降低了加氢产物的凝胶质量分数，制得了氢化度为80%，凝胶质量分数为3.1%的HNBR。