The corrosion resistance of Large-Volume low-quality Fly Ash Concrete (LVFAC) is studied systematically and deeply in this thesis.
本文较系统深入地研究大掺量低质粉煤灰混凝土抗侵蚀性能。
Results indicated that fly-ash substituting same amount of cement can effectively solve the problem of insufficient anti-chloride-corrosion ability of steam cured concrete.
试验结果表明，粉煤灰等量取代部分水泥，可以有效解决蒸汽养护混凝土抗氯离子侵蚀能力不够的问题。
Based on the method of linear polarization, AC impedance and time potential, it is studied that the properties of seawater corrosion resistance of rebar in normal concrete and fly ash concrete.
应用线性极化法、交流阻抗法和时间电位法等电化学方法对普通混凝土和掺粉煤灰混凝土中钢筋耐海水侵蚀性能进行了研究。
The result shows that high content fly ash active powder concrete has small volumetric shrinkage and excellent anti-carbonization resistance to penetration of chlorine ion and to sulfate corrosion.
研究结果表明，大掺量粉煤灰活性粉末混凝土具有较小的体积收缩率，抗碳化、抗氯离子渗透、耐硫酸盐浸蚀性优异。
On the condition of long time seawater corrosion, the hydroxide ion diffusion coefficient and the chlorion diffusion coefficient of fly ash concrete are far smaller than th...
在长期海水侵蚀下，掺粉煤灰混凝土的氢氧离子扩散系数的氯离子扩散系数亦均远小于基准混凝土。
On the condition of long time seawater corrosion, the hydroxide ion diffusion coefficient and the chlorion diffusion coefficient of fly ash concrete are far smaller than th...
在长期海水侵蚀下，掺粉煤灰混凝土的氢氧离子扩散系数的氯离子扩散系数亦均远小于基准混凝土。