Transparent fireproof coating for wood based on melamine-formaldehyde resin as raw materials has good decorating property and fireproof property as well.
以三聚氰胺-甲醛树脂为原料的木材透明防火涂料,具有良好的装饰性能和防火性能。
A transparent dilatant fireproof coating was prepared, based on a modified urea-formaldehyde resin as binder, and phosphoric acid and starch as fire retardant.
以改性脲醛树脂为基料,磷酸和淀粉为阻燃剂制得膨胀型透明防火涂料。
A transparent dilatant fireproof coating was prepared, based on a modified urea-formaldehyde resin as binder, and phosphoric acid and starch as fire retardant.
前言:以改性脲醛树脂为基料,磷酸和淀粉为阻燃剂制得膨胀型透明防火涂料。
Two terminal extensions are fixd on both ends of a ceramic tube on whose surface winds wave-shapcd alloy resistance wire and a high temperature-resistant and fireproof coating are applied.
在圆柱形的瓷管上固定了两个引出端子,陶瓷管表面上缠绕了扁带波浪形状的合金电阻丝,并在其表面涂覆一层具有阻燃,耐高温特性的涂层。
E. g. by ISO 834 curve thawing, fireproof performance reach 3h, general coating thickness need about 20 ~ 30 mm, Due to the coating thicker, requiring multiple coating, construction difficulties.
如按iso 834曲线升温,耐火性能达到3h,一般涂料涂层厚度约需20 ~30mm;由于涂层较厚,需要多次喷涂,施工困难。
E. g. by ISO 834 curve thawing, fireproof performance reach 3h, general coating thickness need about 20 ~ 30 mm, Due to the coating thicker, requiring multiple coating, construction difficulties.
如按iso 834曲线升温,耐火性能达到3h,一般涂料涂层厚度约需20 ~30mm;由于涂层较厚,需要多次喷涂,施工困难。