The interface between the resin and the filler or reinforcement is of utmost importance.
在树脂与填料或增强材料之间的界面是极其重要的。
The composition having at least one epoxy resin, at least one solvent and a filler of functionalized colloidal silica.
该组合物含有至少一种环氧树脂，至少一种溶剂和官能化胶态硅石填料。
The effect of resin coloring, silicone rubber long service life, and by adding substantial filler.
该树脂着色效果好，硅橡胶使用寿命长，并可加入大量填充剂。
This article is mainly about the researching process of a high quality correcting liquid, Discuss the different resin, filler, solvent may lead to the different property of the correcting liquid.
主要介绍一种优质涂改液的研制开发过程，讨论不同的树脂、填料、溶剂的选用对所制得的涂改液性能的影响。
Actual figure dependent on base resin and filler.
实际的数值依赖于基础树脂和填充物。
It consists of special resin, foaming agent fire-proofing agent, carbonic agent, pigment and filler.
由特殊树脂，加上发泡剂、防火剂、成碳剂以及颜填料等组成。
This paper studies chiefly the basic properties of the composite of un-saturated polyester resin in which wollastonite powder is used as a filler.
本文研究了硅灰石填充不饱和聚酯树脂体系的一些基本性能，进而研究了模塑料的配方和性能并压制了绝缘制品。
The first part includes a resin and a particulate filler of a type and amount required to achieve the desired viscosity.
第一部分包括要达到需要的粘度所要 求的类型及数量的树脂和粒状填料。
This article, taking silica as example, mainly discusses filler types and their respective function in package resin, as well as its influence on package resin performance.
文章主要从封装树脂用填充剂的种类以及在封装树脂中的作用进行阐述，并以二氧化硅为例来研究分析填充剂对封装树脂主要性能的影响。
A study has been carried out about conductivity and mechanical properties of semiconductive composites based on EVA as base resin and carbon black as conductive filler.
本文对以eva为基体树脂，炭黑为导电填料的半导电复合物的物理力学性能及电性能进行了研究。
The color epoxy floor coatings are studied. Epoxy resin, polyamide adduct curing agent, pigments, filler, additives and solvent mixture are used as major material.
以环氧树脂、胺加成固化剂、颜料、填料、助剂和混合溶剂为原料研制了彩色环氧地坪涂料。讨论了各组分对涂料性能的影响。
The encapsulate composite for pulsed piezoelectric power supplier was investigated in this paper, in which a bisphenol A liquid epoxy EP828/E51 was resin matrix and aluminum oxide was filler.
本论文研究的复合封装材料以双酚A型环氧树脂EP828／E51作为基体，以氧化铝作为填充材料，有望替代纯环氧固化物作为脉冲压电电源用新型封装材料。
He product based on phenolic resin as adhesive with mineral filler and other additives is processed into thermosetting plastics.
本产品以酚醛树脂为粘合剂，加入矿物填料及其它添加物而制成的热固性塑料。
Two-component polyurethane synthetic-rubber track resin slurry was prepared by polyether, chain extender, MDI-based polyisocyanate, plasticizer, filler.
以聚醚多元醇、扩链剂、异氰酸酯、增塑剂、填料等为原材料，制备了MDI型双组分聚氨酯塑胶跑道用浆料。
The thermoplastic polycarbonate resin composition may further include about 5 to about 50 parts by weight of a filler (e).
该热塑性聚碳酸酯树脂组合物可以进一步包括约5至约50重量份的填料(E)。
Dental filling materials contain resin of polymer, inorganic filler and photoinitiator system, which are used in dental restoration.
齿科充填复合材料是由高分子基质、无机填料及光引发剂体系组成的复合物，主要用于齿科的修复。
Shrinkage small, directional, high incidence of adverse Weld, deformation, warping, shrinkage cracks and stress concentration, resin filler uneven.
收缩小，有方向性，易发生熔接不良，变形、翘曲、缩孔、裂纹及应力集中，树脂填料分布不匀。
When the content of SiC filler is 80~160 parts by weight(based on 100 parts by weight epoxy resin) the compressive strength has higher values and the bonding strength also has better level.
当碳化硅填料的质量份数在80～ 16 0 （相对于环氧树脂10 0份）时，压缩强度达到较高值，粘接强度也保持在较好水平。
The effect of resin coloring, silicone ruber long service life, and by adding substantial filler.
该树脂着色效果好，硅橡胶使用寿命长，并可加入大量填充剂。
Spread at least one coating on at least one surface of sandwich layer, contain the resin in the coating and the filler bead of 50% volume at least.
在芯层的至少一个表面上涂上至少一个涂层，涂层中含有树脂和至少50%体积的填料颗粒。
The method includes adding a long fiber filler to a polyester resin to form a master batch, and blending the master batch and a polycarbonate resin.
所述方法包括将长纤维填料加入到聚酯树脂中以形成母料，并将所述母料与聚碳酸酯树脂共混。
The light filler (2) is formed by the mixing of regenerated cotton fiber and resin adhesive.
所述的轻质填充物(2)由再生棉纤和树脂胶混合而成。
The effect of base resin, content of filler and coupling agent on thermalstability of non halogen flame retardant polyolefin composite were studied in this paper.
研究了树脂基体、填料含量和偶联剂对无卤阻燃聚烯烃复合材料体系热稳定性的影响。
Compared with the traditional composite resin, the content of filler in flowable resin is lower, resulting in its different performances.
流动树脂与传统复合树脂相比，填料含量较低，各种性能也随之改变。
The bipolar plate is made from a composition containing at least epoxy resin, graphite filler and a metal amine complex compound taken as an epoxy resin curing agent.
一种双极板，由包含至少一种环氧树脂、石墨填充物以及作为环氧树脂固化剂的金属胺络合物的组合物制成。
This article makes a deep study of formulated JN-90 low toxic urea-formaldehyde resin with different filler and extender and manufactured board using different tree species veneer.
就JN—90低毒性脲醛树脂胶铁调胶与不同树种单板的制板工艺进行了深入研究。
Composite resin is a kind of dental material composed of resin martrix, pre-treated filler and initiating system which has been widely used in dental restoration.
复合树脂是一种由有机树脂基质和经过表面处理的无机填料以及引发体系组合而成的牙体修复材料。广泛用于各类牙体缺损的直接和间接修复。
Results show that final molar ratio of DFK resin and spread affected boiling peel percentage significantly, filler has no effect on it. More ideal parameters of cold-press process...
结果表明，DF K树脂的终摩尔比和涂胶量对煮沸剥离率的影响最显著，填料添加量影响甚微，并确定了较为理想的冷压胶合工艺参数。
Results show that final molar ratio of DFK resin and spread affected boiling peel percentage significantly, filler has no effect on it. More ideal parameters of cold-press process...
结果表明，DF K树脂的终摩尔比和涂胶量对煮沸剥离率的影响最显著，填料添加量影响甚微，并确定了较为理想的冷压胶合工艺参数。