This paper gives a comprehensive failure analysis on the thermal fatigue crack of engine exhaust manifold and makes an improvement for materials and structures.
对某车型发动机排气歧管的热疲劳断裂问题进行综合失效分析，并从材料、结构方面提出改进意见。
Through the comprehensive analysis, the result shows that crack failure reason is embrittlement of the austenite stainless steel at high temperature.
通过综合分析指出对流管发生失效的原因是奥氏体不锈钢长期在高温下工作引起的热脆化开裂。
Some in-site vibrating test and metal fracture analysis have been done to reveal that the crack of the U-shaped bolts is fatigue failure and some reference for designer is put forward.
结合桥梁—人行道系统的现场振动测试和螺栓试样断口分析结果，指出既有桥上发生的U型螺栓破断属于疲劳破坏，并提出了改进意见。
Based on the failure analysis of reinforced concrete and the fracture behavior of concrete as a type of quasi-brittle materials, a model of matrix crack with bridging bar is proposed in this paper.
基于钢筋混凝土的破坏分析，结合混凝土类准脆性材料的断裂特性，本文提出了强化筋桥联基体裂纹力学分析模型，在该虚拟裂纹端部存在粘聚力分布，而强化筋在桥联裂纹处具有与基体脱离的部分段。
Based on the model, a failure probability analysis method of crack growth is presented which takes the randomness of inclusions' position into consideration.
在此基础上提出的裂纹扩展失效概率分析方法，能考虑夹杂空间位置随机性及扩展过程中的裂纹合并情况。
In response to the complexity of calculation for failure probability regarding fatigue crack growth life, a method for reliability analysis based on neural network response surface was presented.
针对疲劳裂纹扩展寿命失效概率计算的复杂性，提出基于神经网络响应面的可靠性分析方法。
According to the images of coal deformation and failure, obtained the forms of deformation and failure of coal and the Variation of crack parameters by analysis.
根据煤体变形破坏图像，分析得出了煤体破坏形式，以及裂纹参数变化规律。
The integrated analysis of crack failure for L-B Composite Brake Beam Bar Flange Slab was made by means of SEM, microscope and chemical analysis.
采用残余应力和力学性能测定、化学成分分析、断口扫描及金相检验等方法对铁路货车用l - B型组合式制动梁撑杆翼板产生裂纹的原因进行了分析。
Abstract: Through hardness testing, metallographic microscope analysis, and other means, the origination of crack failure of the aluminum alloy die casting die was analyzed.
摘要：通过硬度测试、金相组织观察，研究分析了铝合金压铸模具发生早期龟裂失效的原因。
Abstract: Through hardness testing, metallographic microscope analysis, and other means, the origination of crack failure of the aluminum alloy die casting die was analyzed.
摘要：通过硬度测试、金相组织观察，研究分析了铝合金压铸模具发生早期龟裂失效的原因。