It was indicated that the linear defect appeared after machining is not crack, it is the appearance of oxide film involved in the casting under the effect of external force.
结果表明，这种加工后出现的线性缺陷并非裂纹，而是卷入铸件的氧化膜受外力作用后在叶片表面的显现。