It shows that the main causes of lining wear in ferro - chrome smelting process are the chemical erosion by early slag and the thermal effect at high temperature.
指出在冶炼过程中炉衬遭损坏的主要原因是初渣的化学侵蚀和精炼期的高温热作用。
The estimation of erosion thickness is a foundation for studying palaeostructural characteristic, modeling source rock thermal evolution history and analyzing palaeo-fluid potential.
剥蚀厚度估算是进行古构造特征研究、烃源岩热演化史模拟和古流体势分析的重要基础工作。
The erosion during shutting down do large harm to thermal equipments and effect the safe and economic running of thermal equipment.
停用腐蚀严重影响了机组安全、经济运行,具有较大的危害性。
The wear reason of slit purging plug used in the large refining ladle has been analyzed in detail in the paper, that is the thermal stress and strong erosion and abrasion.
对狭缝式透气砖在大型精炼钢包中的损毁原因进行了分析,热应力和强大的冲刷磨损作用是两个主要因素。
Controlled by the deposition and erosion as well as the basin thermal evolution, the hydrocarbon generation was of multi-phases.
受沉积剥蚀及盆地构造—热演化的控制,生油岩系的生烃阶段与过程具有多期次的特征。
This paper analyses the mechanism of corrosion and its prevention about metal gates, and expounds the application of thermal spraying in gates against erosion.
本文通过对金属闸门腐蚀机理和防腐机理的分析,阐述热喷涂工艺在水工闸门防腐中的应用。
In hot impression die forging, the principal modes of die failure are erosion, thermal fatigue, mechanical fatigue and permanent (plastic) deformation.
在热压模缎中,模具失效的主要模式是腐蚀作用、热疲劳、机械疲劳和永久性即塑性变形。
The performance valuation and analysis was reviewed to the mechanics property, oxidation resistance, hot corrosion resistance, erosion resistance, and thermal property of thermal barrier coatings.
文中对热障涂层的力学性能、抗氧化和抗热腐蚀、抗磨蚀和热学特性等性能的评价及性能判断与分析进行了综合回顾。
The ablation mechanisms of components are particles erosion and mechanical denudation. Material failure is mainly caused by the thermal stress.
同时,材料所受到的热应力是引起材料失效的主要原因。
The performance index shows shat obsolute AZS materials can increase the thermal shock performance of the bricks, and have good erosion-resisting and erosion-flushing characteristics on h.
结果表明,电熔AZS回收料的引入,增大了基质的高温黏度,改善了制品高温显微结构,有利于制品热震性能的提高,并对高钙渣系具有良好的抗冲刷性能以及抗侵蚀性能。
The performance index shows shat obsolute AZS materials can increase the thermal shock performance of the bricks, and have good erosion-resisting and erosion-flushing characteristics on h.
结果表明,电熔AZS回收料的引入,增大了基质的高温黏度,改善了制品高温显微结构,有利于制品热震性能的提高,并对高钙渣系具有良好的抗冲刷性能以及抗侵蚀性能。