Alkyd paints may have reduced adhesion to Star Marine Epoxy Mastic NTC.
如果复涂以醇酸漆,将有可能降低配套体系的附着力。
Alkyd paints may have reduced adhesion to Star Maling Epoxy Mastic Hold.
如果复涂以醇酸漆,将会存在降低配套体系附着力的问题。
Based on this, QS toughener was added to form epoxy resin alloy of "sea island structure", thus further improving its adhesion.
在此基础上加入QS型增韧剂,形成具有“海岛结构”的环氧树脂合金,粘结性能进一步提高。
A cashew shell oil modified epoxy phenolic paint has been developed, which can be applied on the untreated polypropylene surface with good adhesion, high hardness, fast curing and glass.
采用腰果壳油改性环氧酚醛树脂漆,对不经表面处理的聚丙烯塑料坯胎进行涂饰,具有良好的附着性、干性、硬度和光泽。
The influence of acrylate and epoxy resins on the adhesion properties of modified PF resin was studied.
考查了丙烯酸酯单体种类、用量以及环氧树脂用量对改性酚醛树脂粘接性能的影响。
Epoxy - polyurethane IPN anticorrosive paint forms film with excellent anticorrosive property and adhesion.
研制的环氧-聚氨酯互穿网络(IPN)防腐蚀涂料具有优异的防腐蚀性能和附着力。
Star Maling Epoxy Mastic Hold is a high build coating with excellent adhesion to steel, aluminium and most aged coatings.
本产品是厚浆型涂料,对钢材、铝材和大部分旧涂层有非常好的附着力。
In this paper, studied the hydrolysis character of silane coupling agent and the adhesion between the iron-steel substrate and epoxy coatings which blended silane coupling agent.
本文对硅烷偶联剂的水解特性,以及对硅烷偶联剂直接添加到环氧涂料中形成的涂层与钢铁基材的附着力进行了研究。
Addition of flexible epoxy resin QS-310N reduced the curing rate and adhesion could also be improved.
加入柔性环氧树脂QS 310n后固化反应速度有所降低,粘结性能亦有提高。
The influence of WD-60 coupling agents on adhesion and salt-spray property of epoxy anti-corrosive coating were investigated.
研究了WD-60偶联剂对环氧防腐涂料附着力和耐盐雾腐蚀性能的影响,确定了WD-60偶联剂的最佳用量。
An UV curable corrosion resistant coating consists of an epoxy-base monomer, combined active diluents with hydroxy groups, combined photoinitiators, an adhesion promoter.
所研究的UV固化防腐蚀涂料包括环氧类的单体,带羟基功能团的复合稀释剂,复合光引发剂和粘附力促进剂。
Through performance research of FYT, SBS modified bitumen and epoxy asphalt, shearing stress, drawing stress and aging performance of three water proofing and adhesion material have been compared.
通过对SBS改性沥青、环氧沥青、FYT桥面二涂防水粘结材料三种防水粘结材料的性能研究,对比了三种防水粘结材料的剪切强度、拉拔强度和老化性能。
The adhesion measurements results showed that the epoxy coatings can adhere to 304 stainless steel, the adhesion of all samples reached grade 2.
涂层附着力的测定表明:环氧树脂能与304不锈钢很好的结合,该涂层的附着力达到2级。
The adhesion measurements results showed that the epoxy coatings can adhere to 304 stainless steel, the adhesion of all samples reached grade 2.
涂层附着力的测定表明:环氧树脂能与304不锈钢很好的结合,该涂层的附着力达到2级。