The results show that interface element diffusion and reaction on interface in vacuum hot-pressing sintering processing improved interface strength. Fracture occurred mainly in Al matrix.
结果表明，真空烧结过程中出现了界面反应，改善了界面结合强度，断裂破坏主要在基体上进行。