The chemical composition of the interfacial phase was analyzed by EDAX.
用x -射线能谱仪测定了界面相的化学成分。
SEM-EDAX was employed to study the morphology and composition of tobermorite.
用SEM - EDAX研究了雪硅钙石的形貌和成份。
The forming mechanism of the gypsum ceramic is investigated by XRD, SEM - EDAX methods.
用XRD、SEM- EDAX等测试手段研究了石膏陶瓷的形成机理。
The structure and composition of the cuticle of sugarcane stem were studied by means of SEM EDAX.
用SEMEDAX法研究蔗秆表皮层的超微结构及元素组成。
The surface inclusion in cast rolling aluminum strip was observed and analyzed by means of SEM and EDAX.
采用SEM和EDAX分析技术,观察和分析了铸轧铝带的表层夹杂缺陷。
The microstructure of MDF cement and its fracture surface were investigated in detail by SEM/EDAX, STEM et al.
应用SEM/EDAX、STEM等仪器比较详细地研究了MDF水泥及其断口的微观结构。
The joint structure and element distribution at brazing seam are also studied by SEM/EDAX and thermodynamics measures.
通过SEM/EDAX以及热力学方法分析了钎焊接头组织及钎缝的成分分布。
The microstructure and the phase composition of the alloy were analyzed through optical microscopy, SEM, EDAX and XRD techniques.
通过光学显微术、SEM、EDAX、XRD技术分析了热等静压对材料的显微组织和相成分的影响。
The microstructure and mechanic performances of the coating were tested by SEM, XRD, EDAX, microhardness tester and other equipments.
使用扫描电镜(SEM)、X射线衍射(XRD)、X射线能量色散谱仪(EDAX)、显微硬度仪等设备检验了涂层的组织和性能。
The interface between implant and bone were observed with scanning electron microscope (SEM) and X ray energy spectrum analysis (EDAX).
对种植体骨界面作扫描电镜观察、X线能谱分析。
The morphological structure of moggy guard fur was observed by SEM. The elements in squama, cortex and medulla were also analyzed by EDAX.
本文对家猫针毛的形态结构进行了扫描电镜(SEM)观察,并且利用X射线能谱仪(EDAX)分别对鳞片层、皮质层和髓质层进行了元素分析。
The intermetallic compounds (IMCs) between copper and gold and between copper and aluminum are identified on the fractured surfaces by EDAX.
确定的断裂表面的EDAX(介金属化合物)之间的铜和金,铜和铝之间的金属间化合物。
In this paper a macro-cracking in the medium casing which is a heavy section casting of 261 turbogenerator was investigated by SEM, EDAX and others.
采用扫描电镜断口分析、微区能谱分析等方法研究了261汽轮机中汽缸大型铸件开裂问题。
Microstructural homogeneity of a rebonded magnesia-chrome brick used in tunnel kiln in a period of 10 years were studied by means of OM, SEM, EDAX and XRD.
利用OM、SEM、EDAX和XRD检测方法研究了一种在隧道窑烧成带使用10年的再结合镁铬砖显微结构均化现象。
The removal behavior of mineral elements and ash in wheat straw during alkaline pulping is studied by means of atomic absorption spectrometer and SEM-EDAX.
用原子吸收光谱法、SEM - EDAX法研究了麦草原料灰分及矿质元素在碱法制浆过程中的脱除规律。
By means of SEM, EDAX and om, the petrographic structure and microscopic chemical composition of cement clinker have been researched by adding rare-earth lean ore.
采用SEM、EDAX、OM等分析测试方法,研究了稀土贫矿掺加条件下,水泥熟料的岩相结构及其微区化学组成。
The lamellar cracking was found at the specimen of HSLA Nb-V steel plate after tensile strength testing, then the fracture surface of the specimen was studied by SEM and EDAX.
针对高强度低合金铌钒钢板在拉伸试验后出现分层开裂的现象,采用SEM、EDAX进行微观分析,发现试样内部有大量夹杂物存在,这些夹杂物主要含有钙、氧、硫、锰等元素。
The changes in the microstructure and matrix composition of every zone have been investigated by using SEM and EDAX. Also the process and mechanism of slag corrosion have been discussed.
本实验采用SEM和EDAX研究了各段带的显微结构和基质组成,讨论了转炉终渣对浇注料的侵蚀过程和机理。
Electrochemical measurements, corrosion tests, SEM and EDAX were used to investigate forming cerium conversion coatings on aluminum alloys in cerium salt solutions by cathodic electrolysis.
在铈盐溶液中用阴极电解的方法沉积铝合金铈转化膜,用电化学测试、腐蚀实验、SEM和EDAX等分析手段研究了转化膜的性能。
Kao Sung-nien's fat but firm face was like an unleavened millet-flour steamed bread. "Voracious time" (Edax vetustas) could not make a dent on it. There was not a single tooth mark or crease .
高校长肥而结实的脸像没发酵的黄面粉馒头,“馋嘴的时间”咬也咬不动他,一条牙齿印或皱纹都没有。
To know the current status of airborne pollution in Yungang Grottoes, main substantial composition of the deposition of airborne particles is analyzed by means of XRD, SEM (EDAX), and microscope.
为了解云冈石窟大气中粉尘污染的现状,用X射线衍射、扫描电镜(EDAX)和显微镜对大气中粉尘的主要物质成分进行了分析。
Scanning Electronic Microscope(SEM)and EDAX were used to analyze the surface defect of mandril for hot rolling steel tube. Appearance and growth of the surface defect were investigated and discussed.
采用扫描电镜及能谱分析对热轧管用失效芯棒的表面缺陷进行分析,探讨了芯棒表面缺陷的产生原因和长大机理。
Scanning Electronic Microscope(SEM)and EDAX were used to analyze the surface defect of mandril for hot rolling steel tube. Appearance and growth of the surface defect were investigated and discussed.
采用扫描电镜及能谱分析对热轧管用失效芯棒的表面缺陷进行分析,探讨了芯棒表面缺陷的产生原因和长大机理。