While polyester fiber is subject to different draw ratio and heating temperature during high speed spinning, its original molecular orientation and crystallinity of polyester fiber are changed.
聚酯在高速纺丝过程中，施以不同的拉伸倍数与温度，会造成纤维结晶度与取向度的变化，从而影响纤维的物理性能。
The influences of formation condition and draw ratio in melt spinning on the hollowness of Circular cross section hollow polyester fiber are studied.
本文就熔融纺丝成形条件及后拉伸倍数对圆中空聚酯纤维中空度的影响进行了探讨。
Through crossed experiment, the effects of spinning speed, draw ratio, tow temperature at DF3 exit on strength and elongation of 1.
通过正交实验分析了纺速、拉伸倍率、DF3出口处丝束温度对1。
The results showed the influence on fiber strength and elongation at break was in draw ratio, spinning speed, DF3 exit temperature order.
对断裂伸长率的影响依次为拉伸倍率、纺速、DF3出口温度。
Using NaSCN as solvent, acrylic fiber was produced by one-step wet spinning process. The effect of spinneret negative draw ratio on fiber formation was discussed.
采用硫氰酸钠为溶剂，湿纺一步法工艺生产腈纶，探讨了喷丝头负拉伸率对纤维成形的影响。
Fiber formation, appearance and properties at least depended on spin dope concentration, coagulation bath composition and concentration, and post-spinning draw.
分析认为纺丝液的浓度、凝固浴组成与浓度、拉伸对丝纤维的物理与机械性能均有影响。
It is found that the draw performance of IPP monofilaments is greatly promoted in the multi-stage drawing under the same spinning condition. The draw ratio approaches 25 x.
试验发现，在相同的纺丝条件下，多级拉伸大大提高了IPP单丝的拉伸性能，拉伸倍数可达25倍。
With the chip-drying process, spinning process and draw-texturing process adjusted, the flame-retardant polyester DTY is produced.
通过对阻燃聚酯切片干燥、纺丝和拉伸变形等工艺的调整，生产了阻燃聚酯低弹丝，探讨了影响阻燃聚酯低弹丝生产的主要因素。
With the chip-drying process, spinning process and draw-texturing process adjusted, the flame-retardant polyester DTY is produced.
通过对阻燃聚酯切片干燥、纺丝和拉伸变形等工艺的调整，生产了阻燃聚酯低弹丝，探讨了影响阻燃聚酯低弹丝生产的主要因素。