The nucleation and growth of dislocation loops and voids in quenched face-centred cubic metals have been studied.
本文研究了淬火面心立方金属内位错环和空洞的形核和长大问题。
The microstructural observation near the fracture indicated that dislocations increased in the matrix of the former composite, while obvious dislocation loops were found in the latter.
对拉伸断口附近显微组织的观察表明，前者基体中位错进一步增殖，后者则存在明显的位错环。
The microstructural observation near the fracture indicated that dislocations increased in the matrix of the former composite, while obvious dislocation loops were found in the latter.
对拉伸断口附近显微组织的观察表明，前者基体中位错进一步增殖，后者则存在明显的位错环。