It is found that the surface defect like black stripes appeared in certain surface regions of die-casting wheel hub AM60B magnesium alloy after acid pickling in the anti-corrosion treatment.
在对AM 60 B镁合金轮毂压铸件进行表面耐蚀处理时，发现在前处理酸洗后，表面某些区域会产生黑色条纹状缺陷。
The most common blister defects in zinc alloy die casting were described. The reason for the defect formation was analyzed and an approach to defect decrease was offered.
介绍了锌合金压铸件中最常见的起泡缺陷，分析了起泡产生的原因，提出了解决问题的办法。
The most common blister defects in zinc alloy die casting were described. The reason for the defect formation was analyzed and an approach to defect decrease was offered.
介绍了锌合金压铸件中最常见的起泡缺陷，分析了起泡产生的原因，提出了解决问题的办法。