The results show that high content of impurity elements, segregation along grain boundaries and uneven grain size are main reasons for the surface damage of domestic tungsten targets.
结果显示，杂质元素的含量偏高和沿晶界的偏析以及不均匀的钨晶粒是造成国产钨靶表面损伤的主要原因。