The results of tension tests show that tensile strength of the LIPNs increases with increasing the contents of PEMA and DAAM-ADH.
拉伸实验结果表明,增加硬组分和交联剂的含量,拉伸强度显著增加。
Adoption of this crosslinking mode could markedly improve water resistance, solvent resistance, glossiness and hardness of the film. 6.5w % DAAM out of total monomer mass was preferred.
采用该交联体系,可显著提高涂膜的耐水性、耐溶剂性、光泽度及硬度,DAAM的用量以占总单体质量的6.5%为好。
Studies were made of preparation of acrylic latex coating crosslinked at ambient temperature with diacetone acrylamide (DAAM) as crosslinking monomer and adipic dihydrazide as curing agent.
对以双丙酮丙烯酰胺(DAAM)为交联单体,己二酰肼为固化剂制备室温交联丙烯酸乳胶漆进行了研究。
Studies were made of preparation of acrylic latex coating crosslinked at ambient temperature with diacetone acrylamide (DAAM) as crosslinking monomer and adipic dihydrazide as curing agent.
对以双丙酮丙烯酰胺(DAAM)为交联单体,己二酰肼为固化剂制备室温交联丙烯酸乳胶漆进行了研究。