Ultimate load designs according to the yield-line or strip methods do not guarantee safety against cracking or excessive deformation.
接屈服线法或条带法的极限荷载设计不能完全保证抗裂或防止过度变形。
Structure testing in low magnificution, chemical composition analysis and microstructure examination were used to analyze the edge cracking of strip steel coil.
采用低倍组织试验、化学成分分析及金相检验等方法，对出现边裂的带钢卷进行了解剖分析。
The mechanism and cause of edge cracking defect of hot-rolled strip in Kunming Iron & Steel co.
对昆钢热轧板卷边裂缺陷机理及成因进行了研究分析，提出了相应的预防控制措施，取得了较好的效果。
Using the ANSYS finite element analysis software, thermal analysis and thermal stress analysis of side dam in the strip casting process are carried out to explain the cause of side dam cracking.
采用ANSYS有限元分析软件，分析了侧封板在铸轧过程中温度场和热应力场，由此解释侧封板产生裂纹的原因。
Using the ANSYS finite element analysis software, thermal analysis and thermal stress analysis of side dam in the strip casting process are carried out to explain the cause of side dam cracking.
采用ANSYS有限元分析软件，分析了侧封板在铸轧过程中温度场和热应力场，由此解释侧封板产生裂纹的原因。