Plasma chromizing was achieved on Q235 steel and 45 steel surface and formed high chrome layer.
采用双层辉光等离子渗金属技术先在Q235钢和45钢表面渗入元素铬，形成高铬合金层；
Under controlling technique factors, we have produced high quality chromizing cast-infiltration layer.
通过控制工艺因素，在铸铁件表面获得了质量完好的铸渗层。
Immediate quenching and tempering process of steel T10 after low temperature salt bath chromizing was studied.
研究了T10钢在低温盐浴渗铬后直接淬火并回火工艺。
The wear resistance of hard alloy (YG14) and boronizing layer, boron-chromizing layer for steel 45 was studied.
研究了硬质合金(YG14)和45钢渗硼层、硼铬共渗层的耐磨性。
By observing and analyzing the casting test piece, we have found a metallurgical integrating layer that is made up of chromizing cast-iron alloy layer.
我们还对铸渗质量较好的铸渗试件进行了观察和分析，发现铸铁渗铬合金层与母材结合良好，呈冶金结合。
The results show that a compound layer with good wear-resistance and corrosion resistance can be gained in 304 austenitic steel by chromizing sbusequent solid soluti…
结果表明，304奥氏体不锈钢经渗铬固溶渗氮复合处理后可获得性能优良的复合渗层，且耐磨、耐腐蚀。
The results show that a compound layer with good wear-resistance and corrosion resistance can be gained in 304 austenitic steel by chromizing sbusequent solid soluti…
结果表明，304奥氏体不锈钢经渗铬固溶渗氮复合处理后可获得性能优良的复合渗层，且耐磨、耐腐蚀。