The result indicated the current of hydrogen permeation from chloride bath was smaller than that from sulfate-chloride bath.
结果表明，氯化物体系比硫酸盐-氯化物混合体系渗氢电流小。
The performance of Cadmium plating from ammonium chloride bath and Cd-Ti plating from non-cyanide bath on super high-strength steels were discussed.
对超高强度钢的氯化铵镀镉与无氰镀镉-钛两种防护镀层进行了对比研究。
Nickel iron chromium alloy with nanocrystalline were electrodeposited from chloride bath containing trivalent chromium ions under direct and pulse current.
采用直流和脉冲电沉积方式从三价铬的氯化物镀液中沉积出镍-铁-铬纳米合金镀层。
When two different metals are placed in a fused alkali or alkaline-earth chloride bath, the more readily corrodible metal will deposit on the less corrodible one.
当两种不同的金属放在熔融的碱金属或碱土金属氯化物盐浴中时，较易腐蚀的金属会沉积在较难腐蚀的金属上。
Type 732 cation exchange resin was added in nickel bath to separate nickel ions and other cations, boric acid and chloride ions were then separately titrated by sodium hydroxide and silver nitrate.
采用732型阳离子交换树脂分离镍及其它阳离子后，分别用氢氧化钠和硝酸银滴定硼酸和氯离子。
A method for continuous titration of boric acid and nickel chloride in bright nickel plating bath was presented.
介绍了一种光亮镀镍液中硼酸和氯化镍的测定方法。
Methods:Chloroform being solvent, under bath heat, 4 hydroxymethyl caged bicyclic phosphate acylated with pentanoyl chloride and hexanoyl chloride dividedly.
方法：用氯仿作溶剂，在浴温条件下，4羟甲基笼状双环磷酸酯分别与戊酰氯、己酰氯发生酰化反应。
Concentration of boric acid in bright sulfate zinc plating bath was determined referring to the same method for chloride type zinc plating bath.
将氯化物镀锌液中硼酸的测定方法用于测量光亮硫酸盐镀锌液中硼酸的含量。
Rhodium in rhodium plating bath was determined by spectrophotometric method using potassium iodine and stannous chloride as chromogenic agent .
以碘化钾和氯化亚锡作显色剂，用光度法测定镀铑溶液中的铑。
Nickel - cobalt - phosphorus alloy was proved with high catalytic activity of hydrogen evolution which can reduce the bath voltage and energy loss during electrolysis of sodium chloride.
结果表明，镍-钴-磷合金具有较高的析氢催化活性，有利于降低槽压，减少能耗。
In this paper, three types of bath for trivalent chromium plating are gained: chloride-glycine bath, chloride-U bath and sulfate-oxalic bath.
本文新近研究了一种以甲酸盐-羧酸盐作为络合剂的三价铬电镀新工艺，并对该溶液和镀层进行了性能测试。
In this paper, three types of bath for trivalent chromium plating are gained: chloride-glycine bath, chloride-U bath and sulfate-oxalic bath.
本文新近研究了一种以甲酸盐-羧酸盐作为络合剂的三价铬电镀新工艺，并对该溶液和镀层进行了性能测试。