The influence of welding thermal cycle on structure and properties in grain-coarsening region of X80 pipeline steel was investigated by weld thermal simulation technique and the charpy test.
采用焊接热模拟试验和冲击试验，研究了X80管线钢焊接热循环对粗晶区组织性能的影响。
In this paper, the dynamic fracture toughness measuring method for 921a shipbuilding steel is studied by instrumented Charpy impact test.
本文利用示波冲击试验，对船用921A钢动态断裂韧性的测试方法进行了研究。
The Charpy impact test of base metal, weld and heat affected zone of X80 grade pipeline steel of certain factory was conducted, and its effective grain was researched.
对某厂x 80高钢级管线钢母材、焊缝、热影响区进行了夏比冲击韧性试验，对其有效晶粒进行了研究。
Charpy impact test (V gap) : the specified height of pendulum of the one-time blow to V notched specimens in beam state, test specimen is broken by the impact absorbing energy.
夏比(V型缺口)冲击试验：用规定高度的摆锤对处于简支梁状态的V型缺口试样进行一次性打击，测量试样折断时冲击吸收功的试验。
The amount of energy required to fracture the material by a single blow is measured by means of a Charpy impact test.
单次冲击破坏材料所需的能量通过却贝摆锤冲击测试的方法测得。
The influence of pre-heating temperature on organization and performance of X80 pipeline steel was investigated by weld thermal simulation technique and the instrumented Charpy impact toughness test.
文章分析了自保护药芯焊丝的主要成分及作用，介绍了天津市金桥焊材集团有限公司研制的X80管道钢用自保护药芯焊丝的力学性能试验结果。
By changing the nolch local ion of Charpy impact test specimens studied the effect of nolch location on toughness and cracking process in multi-layer welds.
通过改变焊缝夏比冲击试样的缺口取向，研究了缺口位向对多层焊缝金属韧性及断裂过程的影响。
Via a series of contrast experiments, the machine's main parameters accorded to the international standard of ISO 14556:2000 (e) "Steel-charpy V-notch impact test - Instrumented test method".
通过一系列对比试验，证明主要指标达到国际标准ISO 14556： 2000 (E)《钢材V型缺口冲击试验——仪器实验方法》的要求。
The influence of pre-heating temperature on organization and performance of X80 pipeline steel was investigated by weld thermal simulation technique and the instrumented Charpy impact toughness test.
采用焊接热模拟技术和显微分析方法，研究了回火焊道热处理对X80级管线钢焊接热影响区韧性的影响规律。
The influence of pre-heating temperature on organization and performance of X80 pipeline steel was investigated by weld thermal simulation technique and the instrumented Charpy impact toughness test.
采用焊接热模拟技术和显微分析方法，研究了回火焊道热处理对X80级管线钢焊接热影响区韧性的影响规律。