Steel-bonded cemented carbide powder processed by explosive compaction was successfully bonded to the surface of carbon steel through liquid phase sintering.
采用液相烧结法将爆炸压实后的钢结硬质合金粉末复合在碳钢表面，成功获得覆层材料。
The results show that the two-step method can effectively remove Co on the cemented carbide substrates and obviously roughen the surface of the cemented carbide substrate.
研究表明，两步混合处理法不仅可以有效的去除硬质合金基体表面的钴，而且，还可显著粗化硬质合金衬底。
Cemented carbide is a widely used material for cutting tools, but depositing diamond film onto the surface of the cemented carbide with strong adhesion is very difficult.
硬质合金是一种广泛使用的工具材料，在其表面沉积高附着力的金刚石薄膜时存在着困难。
The advantages of coated cemented carbide tool in dry milling of high-strength steel are demonstrated, and the workpiece surface roughness reaches the level of semi-finishing grinding.
试验结果表明：涂层刀片干铣削高强度钢的加工性能优异，工件加工表面质量达到半精磨水平。
Steel-bonded cemented carbide powders being compacted by explosive compaction were bonded to the surface of carbon steel using liquid phase sintering.
采用液相烧结技术成功地将爆炸压制后的钢结硬质合金粉末复合在碳素钢的表面。
The results showed that the vacuum boronizing pretreatment method effectively reduced the diffusion and mobility of Co in the substrates and obviously roughened the surface of the cemented carbide.
结果表明，真空渗硼预处理不仅可以有效的消除或控制钴在金刚石沉积时的不利影响，而且，还显著粗化硬质合金基体表面。
The creep deformation is seen as the macroscopic consequence of the progressive destruction of cemented solid contact surface between grains.
流变变形被认为是颗粒间固体胶结接触面的破坏过程的宏观表现。
As the increases of calcination temperature, the red mud surface is more rougher, more compact and more cemented.
随着焙烧温度的增大，赤泥表面的粗糙度越明显，结构的致密性越强，并呈现出较强的胶结性。
After passivating cutting edge and polishing surface can amplify cutting property and prolong operating life time of the cemented carbide cutting tools.
硬质合金刀片经过刃口钝化和表面抛光处理后，能增强切屑性能和提高使用寿命。
Steel-bonded cemented carbide powder mixture(TLMW50) processed by explosive compaction was successfully bonded to the surface of carbon steel through liquid phase sintering.
采用液相烧结技术成功地将爆炸压制后的钢结硬质合金混合粉末（对应国家牌号TLMW50）复合在碳素钢的表面。
Results imply that under the same conditions, grinding force and surface quality of nano-metric cemented-carbide is all higher than that of common cemented carbide.
研究结果表明，在相同磨削条件下，纳米硬质合金磨削力高于普通硬质合金，磨削表面质量要优于普通硬质合金。
Cobalt phase was chemically etched to certain depth beneath the surface and porous layer was formed after YG8 cemented carbide had been soaked in aqueous solution of dilute nitric acid.
YG8硬质合金经稀硝酸水溶液化学侵蚀后，表面一定深度内的粘结相钴将被化学刻蚀掉，引起表层疏松。
WC steel-bonded cemented carbide powders being compacted by explosive compaction were bonded to the surface of carbon steel using liquid phase sintering.
采用液相烧结法将爆炸压实后的WC钢结硬质合金粉末复合在碳钢表面，对不同烧结温度下的界面组织和抗剪强度进行了研究。
The filters should be cemented together, thus minimizing the surface reflection losses.
为了尽量减少表面的反射损失，应该把这些滤色镜胶合在一起。
The impact on ground surface caused by cemented filling method when used for mining steeply inclined orebody is different from that by other methods and has its own law.
胶结充填采矿法开采急倾斜矿体对地表的影响与其他采矿方法不同，有着自己的规律。
Grinding performance of the brazed wheel in the surface grinding of cemented carbide is studied.
以硬质合金为加工对象，研究了该砂轮的磨削性能。
Grinding performance of the brazed wheel in the surface grinding of cemented carbide is studied.
以硬质合金为加工对象，研究了该砂轮的磨削性能。