The testing results show that the extrusion casting aluminium piston rods can replace steel piston rods.
包括挤压铸造工艺参数和模具结构参数的选择，连杆用铝合金材料的选配及性能试验，连杆的台架试验等；
Casting aluminium alloy ZL305A is a new shipbuilding material with high strength, good ageing stability, excellent corrosion resistance.
本文介绍研制的新型铸造铝合金zl305a是一种强度高，时效稳定性好，耐蚀性优良的船用新材料。
Failure analysis of parietal cracking in scavenging pump made of die casting aluminium alloy was carried out by means of metallographic examination, SEM analysis and so on.
借助金相显微镜、扫描电镜等分析手段，对压铸铝合金清洗泵腔壁断裂失效的原因进行了分析。
Key technique of casting aluminium strip with electrolytic aluminium liquid is summarized. The choice of technological parameters of smelting and casting and quality control is introduced.
概述了直接利用电解铝液生产铝带卷的关键技术，并对熔炼、铸轧工艺参数的选择，质量的控制进行了全面的分析。
About half of all aluminium castings are made using high-pressure die-casting (HPDC), in which a molten aluminium alloy is injected under pressure into a steel mould, or die.
大约有一半的铸铝工艺是高压模铸(HPDC)，在这种工艺中，通过压力将液态铝合金注入钢模，或模具。
Good quality aluminium-alloy shell casting I produced by pouring test.
通过热态浇注试验，得到了质量良好的铝合金壳体铸件。
Effect of aluminium on the non-metallic inclusion in ZG35 in suspension casting process was studied in production condition, and the mechanism was investigated by modern testing technique.
本文研究了悬浮铸造过程中铝对ZG35中非金属夹杂物的影响(在生产条件下)，并用现代检测技术对其作用机理进行了初步探讨。
The reels have infinite anti-reverse, centrifugal casting brakes, and a solid aluminium body frame.
角子机具有无限反逆转，离心铸造制动器，以及坚实的铝制车身框架。
The hydrogen content and processing edge cracks was one of the important facts that effected the quality of 5005 aluminium alloy casting-rolling strips.
熔体质量和工艺裂边是影响5005合金铸轧产品质量的重要因素之一。
The properties, composition, USES, handling methods and economics of fluxes for aluminium and its alloys have been reviewed, as well as the safety and casting quality.
综述了固态熔剂的性质、成分、使用、处理方法以及熔剂使用的经济效益、安全性和对铸件品质的影响。
A new kind of aluminium alloy with satisfactory resistivity and good casting properties and good mechanical properties for motor rotors with high torque and high slip is found.
为高转矩、高转差率的电机转子找到了一种既满足电阻率要求，又具有好的铸造性能和好的力学性能的铝合金配方。
When the cenosphere fly ash content is lower, the melt is easily delaminated during preparing the cenosphere fly ash reinforced aluminium composites by stir casting technology.
采用液态搅拌法制备漂珠增强铝基复合材料过程中，当颗粒含量较低时，熔体容易分层。
The paper describes the application of laser technology for aluminium alloy casting metal level automatic control and the effect in quantity of slab.
介绍激光技术在铝合金铸造过程中液位自动控制方面的应用，以及对提高扁锭质量的作用。
The solid/liquid phase transformation of ZL201 aluminium alloy in near liquidus semi-continuous casting was simulated using multiscale simulation technique.
用多尺度模拟方法研究了近液相线半连续铸造中的ZL201合金的液/固相变。
Continous casting and extrusion (CASTEX) technology is adopted to produce 6201 electric aluminium alloy rod.
采用连续铸挤工艺生产6201电工铝合金线材。
From quality of melting metal, casting condition and casting equipment, the influence factors of crack in aluminium and its alloy slab ingot were analyzed, some suggestion have been drawn out.
从铝及铝合金的熔体质量、铸造条件和铸造设备三个方面，分析了对铝及铝合金扁锭裂纹影响的诸要素，并提出避免裂纹的措施。
The invention is usable for aluminium and aluminium alloy casting industry.
本发明适用于铝及铝合金铸造行业。
The experiment results show that adding compound purification devices to the electromagnetic continuous casting technology can improve the qualities and properties of aluminium silicon alloy billets.
实验结果表明：在铝硅合金电磁连铸过程中加入复合净化装置是可以提高铝硅合金铸坯的质量及性能的。
The quality control and measures of producing pure copper strip for copper-clad aluminium conductor was represented, when the strips were in casting, rolling and surface treating.
阐述了生产开发铜包铝线用纯铜带在熔铸、轧制、表面处理过程中的质量控制及其措施。
Large area crack appearing on the surface of the aluminium alloy bakeware casting dies causes its early failure.
某厂铝合金烤盘压铸模因模面出现大面积龟裂而早期失效。
The factors including of melting-casting process, extrusion process, die, and extrusion device resulting in the surface streaks of 6063 aluminium alloy profiles were analyzed.
从熔铸工艺、挤压工艺、模具、挤压设备等方面分析了6063铝合金型材在挤压过程中产生表面条纹的原因，并提出了相应的对策。
Aluminium metal level control measures and practice effects during casting are introduced in detail according to the processes of aluminium semi-continuous DC-casting.
结合铝合金半连续铸造的生产工艺，介绍了铸造铝熔体液面的控制措施以及每种控制措施的实践效果。
The characteristics of melting and casting process of 1A20 aluminium alloy were summarized.
总结了1A20铝合金熔铸方面的一些特点。
This paper introduces emphatically a kind of chemical treatment process prior to the coating on the die casting pieces of aluminium-silicon alloy and its film adhesion.
着重介绍一种简单实用的铝硅合金压铸件涂漆前化学处理工艺及其漆膜的结合性能。
The fluid flow phenomena happened in the mould of continuous casting of aluminium alloy was studied by digital particle image velocimetry(DPIV) technology.
利用先进的数字粒子图像测速技术（DPIV）对铝合金板坯连铸过程中结晶器内的流场进行研究。
The service condition of aluminium alloy casting dies are analysed in this paper. The test of vacuum heat treatment process by high pressure gas quenching for the dies have been carried out.
分析了大、中型铝合金压铸模的工作条件，进行了真空高压气冷热处理工艺的试验研究，选出了适宜的工艺参数，并应用于生产。
This paper mainly introduces the research on the substitution of Aluminium bar by rare earth, magnesium and silica alloy on the process of chemical capping to rimmed steel during casting.
文中主要研究稀土镁硅合金替代铝条应用于沸腾钢浇注的化学封顶工艺。
A pressure casting machine includes the metal flow system, while the system also is used in a process for pressure casting of aluminium alloys.
压力铸造机包括金属流动系统，而该系统还处于压力铝合金铸造过程中使用。
The graphite particulate-aluminium matrix composites are developed by compocasting followed by pressure casting.
用复合铸造及压铸法制备了石墨颗粒铝基复合材料。
The graphite particulate-aluminium matrix composites are developed by compocasting followed by pressure casting.
用复合铸造及压铸法制备了石墨颗粒铝基复合材料。