One of key factors to ensure the compression-sensibility stableness of CFRC is the dispersion of short carbon fiber (CF) in cement paste uniformly.
在CFRC的制备过程中,碳纤维的均匀分散是决定碳纤维水泥石及混凝土压敏稳定性的关键问题之一。
The effect of surface isocyanation of carbon fiber on the melting behavior of PA6 in CF/PA6 composites was studied by Differential Scanning Calorimetry(DSC).
利用差示扫描量热仪(DSC)研究了炭纤维(CF)表面异氰酸酯化改性后阴离子接枝尼龙6(PA6)对CF/PA6复合材料中PA6的多重熔融行为的影响。
Polyacrylonitrile carbon fiber (PAN-CF) was tension carbonized at different temperatures and then graphitized.
在不同温度下对聚丙烯腈基炭纤维(PAN CF)进行张力炭化处理并进行高温石墨化。
The steel bar with good electrical conductivity was used as lateral electrode in the making of carbon fiber (CF) electrically conductive concrete for heating.
利用钢筋良好的导电性来制作碳纤维导电发热混凝土的侧面电极,并进行了相关的试验研究。
The flexural strength of carbon fiber reinforced Polytetrafluoroethylene(CF/PTFE) composite increases with the increase of carbon fiber content both in modified and unmodified CF/PTFE composite.
以碳纤维增强聚四氟乙烯(CF/PTFE)复合材料弯曲强度试验结果作为依据,开展CF/PTFE复合材料界面应力的研究工作。
Tests are conducted to study the moisture absorption behavior of carbon fiber reinforced monomer casting nylon(CF/MC nylon)composites in four kinds of media.
本文对碳纤维增强铸型尼龙(CF/MC 尼龙)复合材料在不同吸湿介质中的吸湿行为进行了研究。
Polyacrylonitrile (PAN) fiber, pitch fiber and rayon fiber (RF) are three main kind of crude materials from which we produce carbon fiber (CF) now.
聚丙烯腈(PAN)纤维、沥青纤维和粘胶纤维(RF)是目前生产碳纤维(CF)的三大原料体系。
The poly (neutral red) _ modified carbon fiber (PNR-CF) microelectrode was prepared by means of electrochemical polymerization.
利用电聚合方法制备了聚中性红(PNR)修饰碳纤维微电极。
It shows good matrix-carbon fiber adhesion between the treated CF with fracture surface morphology and PA6. the mechanical property of composite is enhanced compared with pure PA6.
复合材料断面照片显示处理后的碳纤维和基体尼龙6材料有着很好的界面结合。
The electrical resistance variation of the carbon fiber(CF) cement-based composites at the hydration time and after the hydration time were studied in the paper.
研究了碳纤维水泥基复合材料在水化期间及固化后的电阻变化特性。
The electrical resistance variation of the carbon fiber(CF) cement-based composites at the hydration time and after the hydration time were studied in the paper.
研究了碳纤维水泥基复合材料在水化期间及固化后的电阻变化特性。