The results showed that the burst failure of the primary cyclone separator was caused by inadequate material strength resulted from flushing damage and reduced in thickness in large area.
结果表明，一级旋风分离器爆裂是由于其下封头受到冲蚀损伤，壁厚大面积减薄导致材料强度不足所致。
The results showed that the burst failure of the primary cyclone separator was caused by inadequate material strength resulted from flushing damage and reduced in thickness in large area.
结果表明，一级旋风分离器爆裂是由于其下封头受到冲蚀损伤，壁厚大面积减薄导致材料强度不足所致。