This paper discusses the effect of brazing time, brazing temperature, brazing gap and diffusion treatment on the remelt temperature of the brazed joint.
文章讨论了钎焊时间、钎焊温度、钎焊间隙及焊后扩散处理对钎焊接头再熔化温度的影响。
The test samples of brazed diamond tool are prepared by the high-frequency induction brazing technology under the conditions of different brazing time and vacuity.
利用高频感应钎焊技术，在不同的钎焊时间和真空度条件下制备金刚石工具试样，在自制的装置上测试试样单颗金刚石磨粒的剪切破坏力大小。
The influence of brazing temperature and holding time on microstructure and tensile strength was studied.
研究了钎焊温度和保温时间对钎焊接头组织和性能的影响。
The brazing of PCD tools requires exact heating temperature and soaking time.
聚晶金刚石复合片刀具的焊接，严格要求加热温度和时间的参数。
The above-mentioned process and the brazing process can be finished at one time charging furnace.
上述过程可与钎焊过程一次装炉完成。
The temperature and time range of brazing through the wetting experiment were confirmed, and the effect of brazing conditions on the joint strength through the shear experiment was discussed.
通过对钎料润湿性的研究确定钎焊试验的温度和时间范围；通过剪切试验研究了钎焊工艺参数对接头强度的影响。
The results show that when the brazing temperature is lower or the holding time is shorter, the metallurgic reaction is not strong and the connection is not tight;
结果表明，钎焊温度过低或保温时间过短，钎料与母材相互冶金作用较弱，接头性能较差；
This kind of brazing filler metal had a good filling performance, at the same time, sound high-temperature strength and impact toughness can be obtained in the joint.
该钎料不仅具有较好的填缝能力，同时获得的钎缝接头具有良好的高温强度和抗冲击性能。
This kind of brazing filler metal had a good filling performance, at the same time, sound high-temperature strength and impact toughness can be obtained in the joint.
该钎料不仅具有较好的填缝能力，同时获得的钎缝接头具有良好的高温强度和抗冲击性能。