The major results are summarized as follows: the amorphous coatings were prepared by arc spraying technology, the highest amorphous content attainable 65.
主要研究结果如下：采用电弧喷涂方法制备非晶涂层，涂层中非晶含量最高可达65。
The major results are summarized as follows: the amorphous coatings were prepared by arc spraying technology, the highest amorphous content attainable 65.3%.
主要研究结果如下：采用电弧喷涂方法制备非晶涂层，涂层中非晶含量最高可达65.3%。
There is amorphous phase in diffusion layer of the hot-dip La-aluminizing and the content of the amorphous phase increases due to the addition of rare earths la.
热浸镀铝-镧钢的扩散层中存在非晶态相，且稀土镧的添加可使扩散层中的非晶含量增加。
Cd adsorption decreased with increasing of amorphous Al content in soil colloids, which might be due to the high energy exchange sites being occupied by Al ions.
随着无定形铝含量的上升，吸附量下降，这是因为铝离子占据了高能量的吸附位。
The regular variation of crystallization temperature, magnetic ordering temperature and average hyperfine magnetic field of the amorphous alloys with Nb content were observed.
观察到非晶合金的晶化温度，磁有序温度和平均磁超精细场有规律性的变化。
XRD spectra of the films with different oxygen content in the as-deposited and heat-treated states show that the films changed from amorphous to crystalline states due to heat-treatment.
由热处理前后薄膜的X射线衍射（XRD）发现，经过退火处理后薄膜发生了从非晶态到晶态的相变。
Preset layer thickness and laser scanning speed have definitive matching relation to the content of amorphous in the coatings, respectively;
预置涂层厚度及扫描速度分别与涂层中非晶含量存在着一定的匹配关系；
Thereby the purposes of reducing the impurity content in the amorphous strip and increasing the capability.
从而达到降低非晶带材中杂质含量、提高性能的目的。
The Mg-based block amorphous alloy has the advantages of high amorphous formation ability, high Mg content, high strength, good corrosion resistance, and the like.
本发明的镁基块体非晶合金具有高非晶形成能力，镁含量高，强度高，耐腐蚀性能好等优点。
The results indicate that microcrystalline deposit with low phosphorus content has higher hardness, modulus and fatigue resistance than the amorphous deposit with high phosphorus content.
结果表明，低磷微晶镀层较高磷非晶镀层具有更高的硬度、弹性模量和疲劳抗力；
We are looking for amorphous graphite with fixed carbon up t0 90% , low ash content, particle size diameter up to 20 mm.
我们正在寻求无定型石墨，要求碳粉含量达到90%，灰分含量低，颗粒直径达到20毫米。
Because of the effect of energy particles on the amorphous films, ion implantation action was produced and nitrogen content in the surface was increased.
载能粒子对非晶薄膜的作用，产生氮离子注入效应，使表层的含氮量增加。
Because of the effect of energy particles on the amorphous films, ion implantation action was produced and nitrogen content in the surface was increased.
载能粒子对非晶薄膜的作用，产生氮离子注入效应，使表层的含氮量增加。