Cracking resistance of ultra-low cabon Cu-bearing age-hardening steels was studied in this paper by computing, maximum hardness in weld heat-affected zone test and Y-groove cracking test.
采用理论计算、热影响区最高硬度试验和小铁研试验方法研究了超低碳含铜时效钢的抗裂性。
The Charpy impact test of base metal, weld and heat affected zone of X80 grade pipeline steel of certain factory was conducted, and its effective grain was researched.
对某厂x 80高钢级管线钢母材、焊缝、热影响区进行了夏比冲击韧性试验，对其有效晶粒进行了研究。
In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone (HAZ) near bond line in welded joint was low.
在TCS不锈钢前期焊接试验中发现其焊接接头热影响区的冲击吸收功值在熔合线附近较低，原因是接头热影响区晶粒粗大所致。
The variation of microstructure and mechanical properties of the welding heat-affected zone of 2090 Al-Li alloy were investigated by means of the welding thermal, simulated and strain cycles test.
采用焊接热模拟试验方法研究了在焊接热循环和应力-应变循环同时作用下，2090铝锂合金焊接热影响区显微组织和力学性能的变化特征。
The test results show that the flame cutting heat affected zone is wider than machining and lower in hardness.
结果表明，火焰切割试样焊接接头的焊接热影响区比机械加工试样焊接接头的焊接热影响区宽，硬度低；
In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone (HAZ) near bond line in welded joint was low. The reason is coarse grain in HAZ.
在TCS不锈钢前期焊接试验中发现其焊接接头热影响区的冲击吸收功值在熔合线附近较低，原因是接头热影响区晶粒粗大所致。
In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone (HAZ) near bond line in welded joint was low. The reason is coarse grain in HAZ.
在TCS不锈钢前期焊接试验中发现其焊接接头热影响区的冲击吸收功值在熔合线附近较低，原因是接头热影响区晶粒粗大所致。