The main fretting wear mechanism is abrasive wear and adhesion wear.
磨损机理主要为粘着磨损和磨粒磨损。
The bushes and bearing pins of the rubber O ring roller chains were characterized by stress fatigue wear and adhesion wear;
形圈链条中销轴和套筒的磨损主要以疲劳磨损为主,并伴随着粘着磨损;
The wear mechanism of the nano-composite coatings were mainly fatigue wear and that of the pure nickel coating was mainly adhesion wear.
纳米复合镀层的磨损机制以疲劳磨损为主,而纯镍镀层以粘着磨损为主。
The wear morphology is characterized by abrasive wear and adhesion wear with low current while it is characterized by adhesion with high current.
电流较小时具有磨粒磨损和粘着磨损的共同特征,电流较大时以粘着磨损为主。
The wear mechanism of C/C composites in braking have been inquired , they were abrasion, delamination of part of the friction film, oxidation wear and adhesion wear.
探讨了C/C复合材料的磨损机理,主要有磨粒磨损、剥层磨损、氧化磨损、粘着磨损。
In the construction process of oil and gas drilling, the joint drill wear, eccentric wear and threaded partial adhesion caused drilling damage and then evolved into the major mine accidents.
在石油天然气钻井施工过程中,常常造成钻具接头磨损、偏磨及丝扣粘连,这是引起钻具损坏进而演化为井下事故的主要原因之一。
Adhesion, wear and corrosion resistance of the coatings obtained were compared with those of conventional bluing at room temperature.
测量了发蓝膜的附着力、耐磨和耐蚀性,并与传统常温发蓝进行了对比。
The wear mechanism was abrasive wear and adhesion transfer of the counter-parter when the volume content of PTFE was high.
当PTFE含量较高时,磨损机理除了磨粒磨损外还有对偶件的粘着转移。
The wear mechanism involves adhesion.
其磨损机理表现为粘着磨损。
The main wear mechanisms are adhesion, diffusion and fatigue.
磨损机理主要是粘结磨损、扩散磨损以及疲劳磨损。
The experimental results showed that the blackening film possessed strong adhesion, uniformity in color, excellent luster and better corrosion-and wear resistance.
结果表明:该工艺着色时间短、环境污染小、黑膜附着力强、光泽性好;
The wear of aluminum matrix composites, which is the common result of spall, adhesion and particle wear, is analysed in the end of the paper.
最后分析了铝基复合材料表面的磨损情况,说明了它的磨损是剥落、粘着和磨粒磨损共同作用的结果。
The adhesive condition of wheel and its effects on the wheel wear are analyzed, and the restraint measures of wheel adhesion is proposed.
分析了磨削中的砂轮粘附情况及其对砂轮磨损的影响,提出了抑制砂轮粘附的措施。
Good wear resistance, good adhesion, directly in the waterproof layer in the plaster, leveling and paste the tiles of various finishes.
耐磨性好,粘结性佳,可直接在防水层在抹灰,找平和粘贴各种饰面瓷砖。
Wear mechanism transferred from server abrasive to adhesion with the increasing of hardness of the composites.
随复合材料硬度的增加,磨损机理由严重磨粒磨损向轻微磨粒磨损转变。
With good wear resistance and corrosion resistance, micro-cracks criss-cross network to strengthen the film's adhesion.
纵横交错的微裂纹网络,增强油膜的附着能力。
The results show that electroless nickel copper phosphorus alloy deposits obtained have improved corrosion resistance, appearance, adhesion, porosity, deposition rate, hardness and wear resistance.
结果表明,所得镍-铜-磷合金镀层的耐蚀性、外观、结合力、孔隙率、沉积速度、硬度和耐磨性等性能优于镍-磷合金及前人制得的镍-铜-磷合金镀层。
It contains extreme-pressure, anti-wear, anti-corrosion and adhesion additives.
同时含有抗极压、抗磨损、防腐蚀和增粘添加剂。
It is shown that the horn made of aluminum alloys (e. g. Ly12CZ) is apt to adhesion-wear, that makes the resonance properties worsening and leads to decreasing of the acoustic transmitting efficiency.
表明硬铝合金焊头极易发生表面的粘着磨损破坏,使得声学系统谐振特性变坏,效率降低。
It is shown that the horn made of aluminum alloys (e. g. Ly12CZ) is apt to adhesion-wear, that makes the resonance properties worsening and leads to decreasing of the acoustic transmitting efficiency.
表明硬铝合金焊头极易发生表面的粘着磨损破坏,使得声学系统谐振特性变坏,效率降低。
应用推荐