结果表明，黄铜表面出现点蚀时，电极的极化电阻明显下降，腐蚀电位也明显降低。
The results show, when pitting corrosion occurred on the brass surface, the polarization resistance of electrode was obviously decreased, and the corrosion potential being also obviously lowered.
结果表明，黄铜表面出现点蚀时，电极的极化电阻明显下降，腐蚀电位也明显降低。
The results show, when pitting corrosion occurred on the brass surface, the polarization resistance of electrode was obviously decreased, and the corrosion potential being also obviously lowered.