研究了合金高温退火处理后的组织和性能变化。
Effect of high temperature annealing on corrosion property of cathode aluminium foils;
结合氧化铝模板制约生长技术和高温退火处理，得到了相当统一的多壁碳纳米管。
Highly uniform multiwall carbon nanotubes (MWCNTs) were synthesized using template confining growth technique in combination with high temperature annealing.
采用铟锡合金靶(铟锡，90 -10)，通过直流反应磁控溅射在玻璃基片上制备出ito薄膜，并在大气环境下高温退火处理。
Tin doped indium oxide (ITO) films were deposited on glass substrates by reactive magnetron sputtering using a metallic alloy target (in Sn, 90 10).
经高温扩散退火处理后，显微硬度均匀性显著提高。
Uniformity of microhardness improved significantly after high temperature diffusion annealing.
如果CroMo框架焊后不热处理，关节受高温焊接过程中退火或正常化。
If a CroMo frame is not heat treated after welding, the joints subjected to heat during the welding process are annealed or normalized.
如果CroMo框架焊后不热处理，关节受高温焊接过程中退火或正常化。
If a CroMo frame is not heat treated after welding, the joints subjected to heat during the welding process are annealed or normalized.