比饱和磁化强度随退火温度的升高逐渐增大。
Special saturation magnetization increases gradually with the increase of annealing temperature.
而饱和磁化强度随时效温度的升高而略有下降。
While, the saturation magnetization decreases slightly with increasing aging temperature.
随焙烧温度的升高,矫顽力下降,而饱和磁化强度升高。
With increasing annealing temperature, the coercivity Hc decreases and the saturation magnetization Ms increases.
随着复合纤维中合金含量的增加,饱和磁化强度增大,而矫顽力下降。
With the alloy content in the composite fibers increased, the saturation magnetization increases, while the coercivity decreased.
燃煤飞灰饱和磁化强度与其中的磁性当量铁相对含量存在明显的正相关性。
The positive correlation between equivalent magnetic iron oxide content and saturation magnetization of coal-fired fly ash is significant.
掺杂后钡铁氧体饱和磁化强度较未掺杂钡铁氧体有所提高,矫顽力则显著下降。
In comparison with undoped barium ferrite, saturation magnetization of samples increased and intrinsic coercivity decreased remarkably.
试样的饱和磁化强度为1.79T,接近相同成分下合金的理论磁化强度的数值。
The saturation magnetization of the sample is 1.79T close to the theoretical value of the same composition alloy.
在高密度数据存储应用中,所述强磁材料区含有高饱和磁化强度的纳米磁性微粒。
In the application of high density data storage, the strong magnetic material section contains nanometer magnetic particulate with high saturation magnetization.
目的探讨葡聚糖氧化铁磁性纳米颗粒的制备对其有效粒径和比饱和磁化强度的影响。
Objective To investigate the effect of preparation conditions on the effective diameter and saturation magnetization of dextran magnetic iron oxide nanoparticles.
这是由于材料中的顺磁相在低温时变成铁磁相,使两相的饱和磁化强度差减小的结果。
This fact is duo to the transition to ferromagnetic phase from paramagnetic phase and to the reduction of the difference of magnetization.
纳米复合永磁材料兼具硬磁性相的高矫顽力和软磁性相的高饱和磁化强度,磁性能优异。
Nanocomposite permanent magnet exhibits excellent magnetic properties combining high coercivity of permanent magnetic phase with high saturation magnetization of soft magnetic phase.
随着温度的上升,燃煤飞灰饱和磁化强度在保证煤粒充分燃烧温度范围内有逐渐降低的趋势。
Saturation magnetization of coal-fired fly ash decreases with increasing temperature in the temperature range in which complete burning of coal can take place.
并对制得的二酯基磁性液体饱和磁化强度、密度、粘度、稳定性和粒子直径等性能参数进行表征实验。
The experiments were carried on the synthesized diester-based magnetic fluids to characterize their saturation magnetization, density, viscosity, stability and the diameter of particles.
随成型压力的增加,当保压一定时间、添加一定量助烧剂时,生坯密度随之增加,饱和磁化强度也相应提高。
With the increase of molding pressure, holding pressure for certain time and adding a certain amount of boric acid doping, the compact density and saturation magnetization correspondingly increase.
该造影剂毒性低,生物相容性好,在血液中的半衰期达30 ~60分钟,时间窗口大,且饱和磁化强度大。
The contrast agent has low toxicity, good biocompatibility, large time window and high saturation magnetization, and the half-life period of the contrast agent in the blood reaches 30 to 60 minutes.
该造影剂毒性低,生物相容性好,在血液中的半衰期达30 ~60分钟,时间窗口大,且饱和磁化强度大。
The contrast agent has low toxicity, good biocompatibility, large time window and high saturation magnetization, and the half-life period of the contrast agent in the blood reaches 30 to 60 minutes.